ABSTRACT
In continuous casting processes, inevitable voids (damage) are generated inside the material. The subsequent forming process of hot flat rolling offers the potential of healing these defects by closing the voids and bonding the internal surfaces. In this paper, different forming conditions from hot flat rolling process were characterized with micromagnetic measurement techniques and the influence of the damage evolution on the fatigue behavior was investigated. To characterize the reduction of voids through hot flat rolling processes, nondestructive testing techniques are required. Therefore, micromagnetic measurements such as Barkhausen noise, incremental permeability, and harmonic analysis were carried out, correlated with the number of voids, and compared with each other. The influence of damage evolution of different forming conditions on the fatigue behavior was characterized based on instrumented constant amplitude and multiple amplitude (load increase) tests. A significant increase in fatigue strength due to the hot flat rolling process, which leads to a reduction in the number of voids, was observed. In addition, the fracture surfaces of the specimens were analyzed in the scanning electron microscope.
ABSTRACT
Due to their high strength-to-weight-ratio, magnesium alloys are very attractive for use in automotive engineering. For application at elevated temperatures, the alloys must be creep-resistant. Therefore, the influence of the operating temperature on the material properties under quasistatic and cyclic load has to be understood. A previous study investigated tensile-tensile fatigue behavior of the magnesium alloys DieMag422 and AE42 at room temperature (RT). The aim of this study was the comparison of both alloys regarding compression, tensile, and compression-compression fatigue behavior. The quasistatic behavior was determined by means of tensile and compression tests, and the tensile-compression asymmetry was analyzed. In temperature increase fatigue tests (TIFT) and constant amplitude tests (CAT), the temperature influence on the cyclic creeping (ratcheting) behavior was investigated, and mechanisms-relevant test temperatures were determined. Furthermore, characteristic fracture mechanisms were evaluated with investigations of the microstructure and the fracture surfaces. The initial material was analyzed in computed tomographic scans and energy dispersive X-ray (EDX) analyses.