Multiscale hierarchical and heterogeneous mechanical response of additively manufactured novel Al alloy investigated by high-resolution nanoindentation mapping.

Smart alloying and microstructural engineering mitigate challenges associated with laser-powder bed fusion additive manufacturing (L-PBFAM). A novel Al-Ni-Ti-Zr alloy utilized grain refinement by heterogeneous nucleation and eutectic solidification to achieve superior performance-printability synergy. Conventional mechanical testing cannot delineate complex micromechanics of such alloys. This study combined multiscale nanomechanical and microstructural mapping to illustrate mechanical signatures associated with hierarchical heat distribution and rapid solidification of L-PBFAM. The disproportionate hardening effect imparted by Al3(Ti,Zr) precipitates in the pool boundaries and the semi-solid zone was successfully demonstrated. Nanomechanical response associated with heterogeneity in particle volume fraction and coherency across melt pool was interpreted from nanoindentation force-displacement curves. The hardness map effectively delineated the weakest and strongest sections in the pool with microscopic accuracy. The presented approach serves as a high throughput methodology to establish the chemistry-processing-microstructure-properties correlation of newly designed alloys for L-PBFAM.

Co-introduction of precipitate hardening and TRIP in a TWIP high-entropy alloy using friction stir alloying.

Tuning deformation mechanisms is imperative to overcome the well-known strength-ductility paradigm. Twinning-induced plasticity (TWIP), transformation-induced plasticity (TRIP) and precipitate hardening have been investigated separately and have been altered to achieve exceptional strength or ductility in several alloy systems. In this study, we use a novel solid-state alloying method-friction stir alloying (FSA)-to tune the microstructure, and a composition of a TWIP high-entropy alloy by adding Ti, and thus activating site-specific deformation mechanisms that occur concomitantly in a single alloy. During the FSA process, grains of the as-cast face-centered cubic matrix were refined by high-temperature severe plastic deformation and, subsequently, a new alloy composition was obtained by dissolving Ti into the matrix. After annealing the FSA specimen at 900 °C, hard Ni-Ti rich precipitates formed to strengthen the alloy. An additional result was a Ni-depleted region in the vicinity of newly-formed precipitates. The reduction in Ni locally reduced the stacking fault energy, thus inducing TRIP-based deformation while the remaining matrix still deformed as a result of TWIP. Our current approach presents a novel microstructural architecture to design alloys, an approach that combines and optimizes local compositions such that multiple deformation mechanisms can be activated to enhance engineering properties.