ABSTRACT
Background: The anterior maxilla is challenging regarding aesthetic rehabilitation. Current bone augmentation techniques are complex and 3D-printed bioceramic bone grafts can simplify the intervention. Aim: A four-teeth defect in the anterior maxilla was reconstructed with a 3D-printed synthetic patient-specific bone graft in a staged approach for dental implant delivery. Methods: The bone graft was designed using Cone-Beam Computed Tomography (CBCT) images. The bone graft was immobilized with fixation screws. Bone augmentation was measured on CBCT images at 11 days and 8 and 13 months post-surgery. A biopsy sample was retrieved at reentry (10 months post-augmentation) and evaluated by histological and micro-computed tomography assessments. The definitive prosthesis was delivered 5 months post-reentry and the patient attended a visit 1-year post-loading. Results: A total bone width of 8 mm was achieved (3.7 mm horizontal bone gain). The reconstructed bone remained stable during the healing period and was sufficient for placing two dental implants (with an insertion torque > 35 N·cm). The fractions of new bone, bone graft, and soft tissue in the biopsy were 40.77%, 41.51%, and 17.72%, respectively. The histological assessment showed no signs of encapsulation, and mature bone was found in close contact with the graft, indicating adequate biocompatibility and suggesting osteoconductive properties of the graft. At 1-year post-loading, the soft tissues were healthy, and the dental implants were stable. Conclusions: The anterior maxilla's horizontal ridge can be reconstructed using a synthetic patient-specific 3D-printed bone graft in a staged approach for implant placement. The dental implants were stable and successful 1-year post-loading.
ABSTRACT
Concave surfaces have shown to promote bone regeneration in vivo. However, bone scaffolds obtained by direct ink writing, one of the most promising approaches for the fabrication of personalized bone grafts, consist mostly of convex surfaces, since they are obtained by microextrusion of cylindrical strands. By modifying the geometry of the nozzle, it is possible to print 3D structures composed of non-cylindrical strands and favor the presence of concave surfaces. In this work, we compare the in vivo performance of 3D-printed calcium phosphate scaffolds with either conventional cylindrical strands or star-shaped strands, in a rabbit femoral condyle model. Monocortical defects, drilled in contralateral positions, are randomly grafted with the two scaffold configurations, with identical composition. The samples are explanted eight weeks post-surgery and assessed by µ-CT and resin-embedded histological observations. The results reveal that the scaffolds containing star-shaped strands have better osteoconductive properties, guiding the newly formed bone faster towards the core of the scaffolds, and enhance bone regeneration, although the increase is not statistically significant (p > 0.05). This new approach represents a turning point towards the optimization of pore shape in 3D-printed bone grafts, further boosting the possibilities that direct ink writing technology offers for patient-specific applications.
Subject(s)
Bone Regeneration , Tissue Scaffolds , Animals , Bone and Bones , Osteogenesis , Printing, Three-Dimensional , Rabbits , Tissue Scaffolds/chemistryABSTRACT
Hydrothermal (H) processes accelerate the hydrolysis reaction of α-tricalcium phosphate (α-TCP) compared to the long-established biomimetic (B) treatments. They are of special interest for patient-specific 3D-printed bone graft substitutes, where the manufacturing time represents a critical constraint. Altering the reaction conditions has implications for the physicochemical properties of the reaction product. However, the impact of the changes produced by the hydrothermal reaction on the in vivo performance was hitherto unknown. The present study compares the bone regeneration potential of 3D-printed α-TCP scaffolds hardened using these two treatments in rabbit condyle monocortical defects. Although both consolidation processes resulted in biocompatible scaffolds with osseointegrative and osteoconductive properties, the amount of newly formed bone increased by one third in the hydrothermal vs the biomimetic samples. B and H scaffolds consisted mostly of high specific surface area calcium-deficient hydroxyapatite (38 and 27 m2 g-1, respectively), with H samples containing also 10 wt.% ß-tricalcium phosphate (ß-TCP). The shrinkage produced during the consolidation process was shown to be very small in both cases, below 3%, and smaller for H than for B samples. The differences in the in vivo performance were mainly attributed to the distinct crystallisation nanostructures, which proved to have a major impact on permeability and protein adsorption capacity, using BSA as a model protein, with B samples being highly impermeable. Given the crucial role that soluble proteins play in osteogenesis, this is proposed to be a relevant factor behind the distinct in vivo performances observed for the two materials. STATEMENT OF SIGNIFICANCE: The possibility to accelerate the consolidation of self-setting calcium phosphate inks through hydrothermal treatments has aroused great interest due to the associated advantages for the development of 3D-printed personalised bone scaffolds. Understanding the implications of this approach on the in vivo performance of the scaffolds is of paramount importance. This study compares, for the first time, this treatment to the long-established biomimetic setting strategy in terms of osteogenic potential in vivo in a rabbit model, and relates the results obtained to the physicochemical properties of the 3D-printed scaffolds (composition, crystallinity, nanostructure, nanoporosity) and their interaction with soluble proteins.