ABSTRACT
OBJECTIVE: The use of lasers to fuse different tissues has been studied for 50 years. As none of these experiments concerned the oral soft tissues, our objective was to assess the feasibility of laser gingiva welding. MATERIALS AND METHODS: Porcine full-thickness gingival flaps served to prepare calibrated samples in the middle of which a 2 cm long incision was closed, either by conventional suture or by laser tissue welding (LTW). To determine the irradiation conditions yielding the best tensile strength, 13 output power values, from 0.5 to 5 W, delivered either at 10 Hz or in continuous wave mode, were tested on six indocyanine green (ICG) concentrations, from 8% to 13% (588 samples). Then, some samples served to compare the tensile strength between the laser welded and the sutured gingiva; the other samples were histologically processed in order to evaluate the thermal damage extent. The temperature rise during the LTW was measured by thermocouples. Another group of 12 samples was used to measure the temperature elevation by thermal camera. RESULTS: In the laser welding groups, the best tensile strength (p<0.05) was yielded by the 9% ICG saline solution (117 mM) at 4.5 W, 10 Hz, and a fluence of 31.3 kJ/cm(2). The apposition strength revealed no statistically significant difference (p<0.05) between the sutured and the laser welded gingiva at 4.5 W, 10 Hz, and 9% ICG solution. The mean temperature was 74±5.4°C at the upper surface and 42±8.9°C at the lower surface. The damaged zone averaged 333 µm at the upper surface. CONCLUSIONS: The 808 nm diode laser associated with ICG can achieve oral mucosa LTW, which is conceivable as a promising technique of gingival repair.
Subject(s)
Gingiva/surgery , Lasers, Semiconductor , Animals , Models, Animal , Sutures , Swine , Tensile Strength/radiation effectsABSTRACT
OBJECTIVE: The aim of this study was to evaluate the effect on dentinal surfaces of diode lasers (810 and 980 nm) at different parameters. MATERIALS AND METHODS: Twenty-four caries-free human impacted wisdom teeth were used. The crowns were sectioned transversely in order to expose the dentin. The smear layer was removed by a 1 min application of ethylenediaminetetraacetic acid (EDTA). Each surface was divided into four quadrants irradiated at a different output power setting for each kind of laser: 0.8, 1, 1.6, and 2 W (energy densities: 2547, 3184, 5092, and 6366 J/cm(2), irradiation speed 1 mm/sec; optical fiber diameter: 200 µm; continuous and noncontact mode). Half of the samples were stained with a graphite paste. All specimens were sent for scanning electron microscopic (SEM) analysis. Pulp temperature increases in additional 20 teeth were measured by a thermocouple. RESULTS: Diode laser irradiations at 0.8 and 1 W led to occlusion or narrowing of dentin tubules without provoking fissures or cracks. The application of graphite paste increased the thermal effects in dentin. Measurements of pulp temperature showed that irradiations at 0.8 and 1 W for a period of 10 sec in continuous mode increased pulp temperature (T ≤2°C). CONCLUSIONS: Diode lasers (810 and 980 nm) used at 0.8 and 1 W for 10 sec in continuous mode were able to seal the dentin tubules. These parameters can be considered harmless for pulp vitality, and may be effective in the treatment of dentinal hypersensitivity.