Effects of Biological and Chemical Degradation on the Properties of Scots Pine Wood-Part I: Chemical Composition and Microstructure of the Cell Wall.

Research on new conservation treatment for archaeological wood requires large amounts of wooden material. For this purpose, artificial wood degradation (biological-using brown-rot fungus Coniophora puteana, and chemical-using NaOH solution) under laboratory conditions was conducted to obtain an abundance of similar samples that mimic naturally degraded wood and can serve for comparative studies. However, knowledge about its properties is necessary to use this material for further study. In this study, the chemical composition and microstructure of degraded cell walls were investigated using FT-IR, XRD, helium pycnometry and nitrogen absorption methods. The results show that biological degradation caused the loss of hemicelluloses and celluloses, including the reduction in cellulose crystallinity, and led to lignin modification, while chemical degradation mainly depleted the amount of hemicelluloses and lignin, but also affected crystalline cellulose. These changes affected the cell wall microstructure, increasing both surface area and total pore volume. However, the chemical degradation produced a greater number of mesopores of smaller size compared to fungal decomposition. Both degradation processes weakened the cell wall's mechanical strength, resulting in high shrinkage of degraded wood during air-drying. The results of the study suggest that degraded wood obtained under laboratory conditions can be a useful material for studies on new consolidants for archaeological wood.

Factors That Affect the Mechanical Strength of Archaeological Wood-A Case Study of 18th-Century Wooden Water Pipes from Bóznicza Street in Poznan, Poland.

Large amounts of archaeological wood are often excavated during groundworks in cities and towns. Part of the unearthed artefacts is usually saved, conserved and then presented in museums. However, if the finding contains several similar objects, some of them could potentially be further employed for some other practical purposes. The research aimed to determine the mechanical performance of the remains of wooden water mains excavated at Bóznicza street in Poznan, Poland and evaluate its potential usefulness for any practical purposes. First, wood density was determined along with its mechanical strength in compression. The density of archaeological wood identified as Scots pine was lower than contemporary pinewood (383 kg × m-3 vs. 572 kg × m-3); therefore, its mechanical properties in compression tests were also lower, as expected, making the wood unsuitable for any practical applications. However, the differences in modulus of elasticity and compressive strength were not justified by the differences in wood density. Further infrared spectroscopy and X-ray diffraction analyses revealed additional differences in chemical composition and cellulose crystallinity between archaeological and contemporary wood. The results indicated the decrease in carbohydrate content and cellulose crystallinity in degraded wood, which, in addition to wood density, apparently contribute to the deterioration in mechanical strength of archaeological wood. The case study of the excavated archaeological wooden pipes shows that they have historical value but are not useful for practical purposes. It also revealed that not only wood density but also its chemical composition and cellulose crystallinity level has a substantial impact on the wood mechanical properties, particularly in compression.