ABSTRACT
(1) Background: The use of high-performance polymers for fixed restorations requires additional studies regarding their adaptability and processing with CAD/CAM technology. This in vitro study aims to assess the marginal and internal fit of PEEK and PEKK materials using microcomputed tomography. (2) Methods: Twenty-four (n = 8) MOD onlays made of PEKK (Pekkton ivory), unmodified PEEK (Juvora medical), and modified PEEK (BioHPP) were investigated. A typodont mandibular left first molar was scanned to achieve 24 resin, 3D printed abutment teeth. The onlays were fabricated with a five-axis milling machine, and after cementation of the specimens, the marginal (MG) and internal gaps (IG) were evaluated at twelve points in the mesio-distal section and thirteen points in the bucco-lingual section using microcomputed tomography. For statistical data analysis, Wilcoxon signed-rank/paired Student t-Test, Mann-Whitney/unpaired Student t-Test, and one-way ANOVA test were applied. (3) Results: Significant differences (p < 0.05; α = 0.05) were reported between the MG and IG for each material for all three polymers and also among two materials in terms of the MG and IG (except Juvora-BioHPP). The highest IG values were recorded in angular areas (axio-gingival line angle) in the mesio-distal section for all the polymers. (4) Conclusions: For all the materials, MG < IG. The type of polymer influenced the adaptability; the lowest marginal and internal gap mean values were recorded for BioHPP. The analyzed polymer used for onlays are clinically acceptable in terms of adaptability.
ABSTRACT
Clear thermoplastic materials have increased in popularity in the dental field due to their various applications, combination of excellent aesthetics, and good biomechanical behavior, but they may be influenced by different environmental conditions. The purpose of the present study was to assess the topographical and optical characteristics of thermoplastic dental appliances materials relative to water sorption. PET-G polyester thermoplastic materials were evaluated in this study. Related to water uptake and desiccation stages, surface roughness was analyzed, and three-dimensional AFM profiles were generated for nano-roughness measurements. Optical CIE L*a*b* coordinates were recorded and parameters like translucency (TP), contrast ratio for the opacity (CR), and opalescence (OP) were derived. Levels of color changes were achieved. Statistical analyses were performed. Water uptake significantly increases the specific weight of the materials, and after desiccation, the mass decreases. Roughness increased after water immersion as well. Regression coefficients indicated a positive correlation between TP and a* and between OP and b*. Studied PET-G materials have a different behavior to water exposure, but for all their specific weight, they increased significantly within the first 12 h. It is accompanied by an increase in the roughness values, even if they continue to be kept below the critical mean surface roughness. On nano-level, 3D images show an increase in inhomogeneity in the network structure of particles. Slight color changes were registered.
ABSTRACT
(1) Background: Considering that the appearance of a dental material is an important factor that contributes to the success of prosthetic restorations. The purpose of this study is to investigate the optical properties and color changes among the layers of three commercial zirconias, to compare the aspect of the polished and glazed surfaces before and after aging and to evaluate the effects of hydrothermal degradation on their aesthetics. (2) Methods: Forty-eight plate-shaped samples were sectioned from presintered blocks of each multilayer translucent zirconia with different Yttrium content: Ceramill Zolid fx ML (5 mol%) = CeZ, STML (4 mol%) = STM, IPS e.maxZirCAD CEREC/in Lab MT Multi (4 mol% + 5 mol%) = IPZ. The samples were sintered according to the recommendation of each manufacturer, and half (24) of them were polished and the other half (24) glazed on one of the surfaces. Each type was equally divided into one control and one aging group, and, for each material, this resulted in four groups (n = 12): polished-control, polished-autoclaved glazed-control, and glazed-autoclaved. The artificial aging was carried out with an autoclave and distilled water at 134 °C, 0.2 MPa for 1 h, and for optical parameters (TP, CR, OP) and color change (ΔE*) measurements on a black and white background in a CIE L*a*b* color system, a spectrophotometer was used. The specimens were evaluated in incisal, cervical, and medium areas on polished and glazed samples before and after the aging stage. Statistical analysis was achieved with a two-way ANOVA test, the unpaired t-test, and the paired t-test. (3) Results: Before and after aging, the mean TP values for polished samples were higher than the glazed ones. After aging, the mean TP values increased for all groups (except polished CeZ), and significant differences were reported for polished STM, IPZ. After LTD, the opalescence registered an increase for almost all groups (except polished CeZ, polished and glazed IPZ-medium area), and significant differences were reported for almost all groups (except STM-incisal, IPZ-cervical, medium areas). The levels of color change were between extremely slight to perceivable. (4) Conclusions: Optical properties of the selected multilayer zirconia were influenced by polishing and glazing as surface treatment and affected by artificial aging (CeZ the least); perceivable color changes for polished STM, IPZ were detected.
ABSTRACT
(1) Background: The study was undertaken to evaluate the surface characteristics, microhardness, and color stability of PEEK materials related to water saturation and in vitro aging. (2) Methods: Custom specimens of unmodified and modified PEEK CAD/CAM materials were investigated: BioHPP, a ceramic reinforced PEEK, and Finoframe PEEK and Juvora medical PEEK, 100% PEEK materials. Forty-eight plates were sectioned in rectangular slices. The specimens were immersed in distilled water at 37 °C for a period of 28 days, and then subjected to aging by thermal cycling (10,000 cycles). Surface roughness was measured with a contact profilometer; nanosurface topographic characterization was made by Atomic Force Microscopy; Vickers hardness measurements were performed with a micro-hardness tester; color changes were calculated. All registrations were made before immersion in water and then subsequently once a week for 4 weeks, and after thermocycling. (3) Results: The studied reinforced and unfilled PEEK materials reached water saturation after the first week of immersion, without significant differences between them. The most affected from this point of view was the reinforced PEEK material. Thermocycling induces a significant increase inmicroroughness, without significant differences between the studied materials. In relation to the nanosurface topography and roughness, the reinforced PEEK material was the least modified by aging. The color changes after 4 weeks of water immersion and one year of simulated in vitro aging ranged from extremely slight to slight, for all materials. (4) Conclusions: Water absorption was associated with a decrease in microhardness. Surface characteristics are affected by water immersion and thermocycling. Perceivable or marked color changes of the materials were not detected during the study.
ABSTRACT
(1) Background: The purpose of this study was to evaluate the differences in terms of surface characteristics (roughness, topography, microhardness) among layers for multi-layered high translucent and super-high translucent zirconia and the influence of finishing and aging on surface characteristics and microstructure. (2) Methods: Three types of translucent multilayer zirconia were evaluated: STML (4Y-TZP); IPS e.maxZirCAD CEREC/in Lab MT Multi (4Y-TZP + 5Y-TZP); CeramillZolidfx ML (5Y-TZP). Ninety-six plate-shaped samples (32 for a material), 16 mm × 14 mm × 1 mm size, were cut with a precision disc, polished on both sides with sand papers and sintered respecting the manufacturer's protocol. Half of the specimens (16) were finished by polishing and the other half by glazing and then equally divided into one control group and one group subject to aging by autoclaving (1 h, 134 °C, 0.2 MPa), resulting in four groups of eight samples, for each zirconia. The specimens were evaluated in three areas: cervical, medium, incisal-of each glazed or polished surface, before and after aging. Tests were performed to determine the surface roughness using a profilometer; the surface topography by an atomic force microscope (AFM) and a scanning electron microscope (SEM). Microhardness was recorded using a microhardness tester. Statistical analyses were performed using two-way ANOVA test, unpaired sample t-Test, paired sample t-Test (α = 0.05) and Pearson's correlation. (3) Results: Before and after autoclaving, for glazed samples significance (p < 0.05) higher surface roughness, respectively lower microhardness in comparison with the polished group was assessed. No significant differences (p > 0.05) were reported between the three areas, on glazed or polished surfaces of a material. Although, after aging an increase in surface roughness was observed both on glazed and polished samples, statistical differences were found for STML (p < 0.05). No significant differences (p> 0.05) concerning microhardness among the same areas, on glazed and polished surfaces, recorded before and after aging, except CeramillZolidfx ML glazed samples. (4) Conclusions: For tested zirconia materials no significant differences among layers were registered regarding surface characteristics. Surface treatment (glazing or polishing) has a significant impact on surface roughness and microhardness. Both before and after aging, the surface roughness values for the glazed samples were higher than for those polished. The super translucent 4Y-TZP material was more affected by aging compared to the super-high translucent 5Y-TZP material. The combined material revealed similarities for each layer corresponding to the microstructure.
ABSTRACT
Considering that the processes of PEEK discoloration caused by either intrinsic or extrinsic factors require elucidation, the aim of this study was to investigate the long-term effect of the combined action of ageing and immersing solutions on the optical properties and color stability of PEEK material, related to surface processing (polishing or glazing). (2) Methods: This study aims to determine the influence of different ageing and staining protocols on optical properties, color changes, and surface roughness of a reinforced PEEK material (bioHPP, Bredent, Senden, Germany). For ageing, specimens were submitted to 5000 cycles in a 55 °C bath and a 5 °C bath filled with distilled water. For staining, thermal cycling was performed in a hot coffee bath (55 °C) and a bath filled with distilled water (37 °C) and in a cold juice bath (5 °C) and a bath filled with distilled water (37 °C). Translucency (TP) and opalescence (OP) parameters were determined, the total color change value (ΔΕ*) was calculated, specimens' surface roughness was analyzed, and statistical analyses were performed. (3) Results: The mean TP values of the studied samples were in the interval of 1.25-3.60, which is lower than those reported for natural teeth or other aesthetic restoration materials. The OP values of PEEK were registered in the range of 0.27-0.75, being also lower than those of natural teeth or other aesthetic restoration materials. OP has a very strong positive relationship with TP. The mean registered Ra values for all subgroups were below 0.13 µm. Artificial ageing and staining in hot coffee proved to increase the roughness values. (4) Conclusions: The glazing of PEEK has a favorable effect on surface roughness and opalescence, irrespective of the artificial ageing or staining protocols. Artificial ageing damages the color stability and roughness of PEEK, regardless of surface processing, and decreases the translucency and opalescence of glazed surfaces. Immersion in hot coffee leads to perceivable discolorations.