ABSTRACT
Tailoring metal oxide photocatalysts in the form of heterostructured photonic crystals has spurred particular interest as an advanced route to simultaneously improve harnessing of solar light and charge separation relying on the combined effect of light trapping by macroporous periodic structures and compositional materials' modifications. In this work, surface deposition of FeOx nanoclusters on TiO2 photonic crystals is investigated to explore the interplay of slow-photon amplification, visible light absorption, and charge separation in FeOx-TiO2 photocatalytic films. Photonic bandgap engineered TiO2 inverse opals deposited by the convective evaporation-induced co-assembly method were surface modified by successive chemisorption-calcination cycles using Fe(III) acetylacetonate, which allowed the controlled variation of FeOx loading on the photonic films. Low amounts of FeOx nanoclusters on the TiO2 inverse opals resulted in diameter-selective improvements of photocatalytic performance on salicylic acid degradation and photocurrent density under visible light, surpassing similarly modified P25 films. The observed enhancement was related to the combination of optimal light trapping and charge separation induced by the FeOx-TiO2 interfacial coupling. However, an increase of the FeOx loading resulted in severe performance deterioration, particularly prominent under UV-Vis light, attributed to persistent surface recombination via diverse defect d-states.
ABSTRACT
Photonic crystal structuring has emerged as an advanced method to enhance solar light harvesting by metal oxide photocatalysts along with rational compositional modifications of the materials' properties. In this work, surface functionalization of TiO2 photonic crystals by blue luminescent graphene quantum dots (GQDs), n-π* band at ca. 350 nm, is demonstrated as a facile, environmental benign method to promote photocatalytic activity by the combination of slow photon-assisted light trapping with GQD-TiO2 interfacial electron transfer. TiO2 inverse opal films fabricated by the co-assembly of polymer colloidal spheres with a hydrolyzed titania precursor were post-modified by impregnation in aqueous GQDs suspension without any structural distortion. Photonic band gap engineering by varying the inverse opal macropore size resulted in selective performance enhancement for both salicylic acid photocatalytic degradation and photocurrent generation under UV-VIS and visible light, when red-edge slow photons overlapped with the composite's absorption edge, whereas stop band reflection was attenuated by the strong UVA absorbance of the GQD-TiO2 photonic films. Photoelectrochemical and photoluminescence measurements indicated that the observed improvement, which surpassed similarly modified benchmark mesoporous P25 TiO2 films, was further assisted by GQDs electron acceptor action and visible light activation to a lesser extent, leading to highly efficient photocatalytic films.
ABSTRACT
Heterostructured bilayer films, consisting of co-assembled TiO2 photonic crystals as the bottom layer and a highly performing mesoporous P25 titania as the top layer decorated with CoOx nanoclusters, are demonstrated as highly efficient visible-light photocatalysts. Broadband visible-light activation of the bilayer films was implemented by the surface modification of both titania layers with nanoscale clusters of Co oxides relying on the chemisorption of Co acetylacetonate complexes on TiO2, followed by post-calcination. Tuning the slow photon regions of the inverse opal supporting layer to the visible-light absorption of surface CoOx oxides resulted in significant amplification of salicylic-acid photodegradation under visible and ultraviolet (UV)-visible light (Vis), outperforming benchmark P25 films of higher titania loading. This enhancement was related to the spatially separated contributions of slow photon propagation in the inverse opal support layer assisted by Bragg reflection toward the CoOx-modified mesoporous P25 top layer. This effect indicates that photonic crystals may be highly effective as both photocatalytically active and backscattering layers in multilayer photocatalytic films.