ABSTRACT
The thermally induced solid state synthesis of soluble organophilic maghemite (γ-Fe(2)O(3)) nanocrystallites is described. The solvent-free one-step synthesis involves the reaction in the melt state of Fe(NO)(3)·9H(2)O and RCOOH (R = C(11)H(23), C(15)H(31)) at 240 °C. The method yields well-crystallized nanoparticles of γ-Fe(2)O(3) functionalized with the corresponding aliphatic acid. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) observations reveal composite particles with faceted magnetic cores and average size of 20 nm, which are well capped with the surrounding organic sheath. The Fourier transform infrared (FT-IR) spectra and thermal analysis suggest a bimodal configuration of the organic shell including chemically coordinated and physisorbed molecules of aliphatic acid. The chemical bonding of the carboxylate groups to the surface iron atoms is also indicated by a paramagnetic doublet with unchanged area in the variable temperature Mössbauer spectra. The spinel γ-Fe(2)O(3) particles exhibit perfect structural and magnetic ordering, including the almost ideal ratio of octahedral to tetrahedral positions (5/3) and very low degree of spin canting, as confirmed by in-field Mössbauer spectroscopy. Magnetic measurements demonstrate the suitable properties required in various (bio)magnetic applications like superparamagnetic behavior at room temperature, high saturation magnetization achievable at low applied fields and suppressed magnetic interactions.