Ceramic Inlays: Effect of Mechanical Cycling and Ceramic Type on Restoration-dentin Bond Strength.

This study aimed to evaluate the bond strength between dentin and five different ceramic inlays in permanent maxillary premolars, with and without mechanical cycling. One hundred permanent maxillary premolars were prepared and divided into 10 groups (n=10) according to the ceramic system (IPS e.Max Press; IPS e.Max CAD; Vita PM9; Vita Mark II; and Vita VM7) and the mechanical cycling factor (with and without [100 N, 2 Hz, 1.2×10(6) cycles]). The inlays were adhesively cemented, and all of the specimens were cut into microbars (1×1 mm, nontrimming method), which were tested under microtensile loading. The failure mode was classified and contact angle, roughness, and microtopographic analyses were performed on each ceramic surface. The mechanical cycling had a significant effect (p=0.0087) on the bond strength between dentin and IPS e.max Press. The Vita Mark II group had the highest bond strength values under both conditions, with mechanical cycling (9.7±1.8 MPa) and without (8.2±1.9 MPa), while IPS e.Max CAD had the lowest values (2.6±1.6 and 2.2±1.4, respectively). The adhesive failure mode at the ceramic/cement interface was the most frequent. Vita Mark II showed the highest value of average roughness. IPS e.max Press and Vita Mark II ceramics presented the lowest contact angles. In conclusion, the composition and manufacturing process of ceramics seem to have an influence on the ceramic surface and resin cement bond strength. Mechanical cycling did not cause significant degradation on the dentin and ceramic bond strength under the configuration used.

Trans-enamel and trans-dentinal cytotoxic effects of a 35% H2O2 bleaching gel on cultured odontoblast cell lines after consecutive applications.

AIM: To evaluate the trans-enamel and trans-dentinal cytotoxic effects of a 35% H(2)O(2) bleaching gel on an odontoblast-like cell lines (MDPC-23) after consecutive applications. METHODOLOGY: Fifteen enamel/dentine discs were obtained from bovine central incisor teeth and placed individually in artificial pulp chambers. Three groups (n = 5 discs) were formed according to the following enamel treatments: G1: 35% H(2)O(2) bleaching gel (15 min); G2: 35% H(2)O(2) bleaching gel (15 min) + halogen light (20 s); G3: control (no treatment). After repeating the treatments three consecutive times, the extracts (culture medium + gel components that had diffused through enamel/dentine discs) in contact with the dentine were collected and applied to previously cultured MDPC-23 cells (50 000 cells cm(-2)) for 24 h. Cell metabolism was evaluated by the MTT assay and data were analysed statistically (alpha = 5%; Kruskal-Wallis and Mann-Whitney U-test). Cell morphology was analysed by scanning electron microscopy. RESULTS: Cell metabolism decreased by 92.03% and 82.47% in G1 and G2 respectively. G1 and G2 differed significantly (P < 0.05) from G3. Regardless of halogen light activation, the application of the bleaching gel on the cultured odontoblast-like cells caused significantly more severe cytotoxic effects than those observed in the nontreated control group. In addition, significant morphological cell alterations were observed in G1 and G2. CONCLUSION: After three consecutive applications of a 35% H(2)O(2) bleaching agent, the diffusion of the gel components through enamel and dentine caused severe toxic effects to cultured pulp cells.