ABSTRACT
Hexanuclear tantalum bromide cluster units [{Ta6Bri12}La6] (i = inner, a = apical, L = ligand OH or H2O) are embedded into SiO2 nanoparticles by a reverse microemulsion (RM) based method. [{Ta6Bri12}Bra2 (H2O)a4]·nH2O (noted TBH) and tetraethyl orthosilicate (TEOS) are used as the starting cluster compound and the precursor of SiO2, respectively. The RM system in this study consists of the n-heptane (oil phase), Brij L4 (surfactants), ethanol, TEOS, ammonia solution and TBH aqueous sol. The size and morphology of the product namely {Ta6Br12}@SiO2 nanoparticles are analyzed by HAADF-STEM and EDS mappings. The presence and integrity of {Ta6Br12} in the SiO2 nanoparticles are evidenced by EDS mapping, ICP-OES/IC and XPS analysis. The optical properties of {Ta6Br12}@SiO2 nanoparticles are analyzed by diffuse reflectance UV-vis spectroscopy, further evidencing the integrity of the embedded {Ta6Br12} and revealing their oxidation state. Both {Ta6Br12}2+ and {Ta6Br12}3+ are found in SiO2 nanoparticles, but the latter is much more stable than the former. The by-products in this RM-based synthesis, as well as their related factors, are also discussed.
ABSTRACT
The development of phosphor devices free of heavy metal or rare earth elements is an important issue for environmental reasons and energy efficiency. Different mixtures of ZnO nanocrystals with Cs2Mo6I8(OOC2F5)6 cluster compound (CMIF) dispersed into polyvinylpyrrolidone matrix have been prepared by very simple and low cost solution chemistry. The resulting solutions have been used to fabricate highly transparent and luminescent films by dip coating free of heavy metal or rare earth elements. The luminescence properties of solution and dip-coated films were investigated. The luminescence of such a system is strongly dependent on the ratios between ZnO and CMIF amounts, the excitation wavelength and the nature of the system. By varying these two parameters (ratio and wavelength), a large variety of colors, from blue to red as well as white, can be achieved. In addition, differences in the luminescence properties have been observed between solutions and thin films as well as changes of CMIF emission band maximum wavelength. This may suggest some possible interactions between the different luminophore centers, such as energy transfer or ligands exchange on the Mo6 clusters.