Nonstoichiometry Defects in Double Oxides of the A2BO4-Type.

Double oxides with the structure of the Ruddlesden-Popper (R-P) layered perovskite An+1BnO3n+1 attract attention as materials for various electrochemical devices, selective oxygen-permeable ceramic membranes, and catalytic oxidative reactions. In particular, Sr2TiO4 layered perovskite is considered a promising catalyst in the oxidative coupling of methane. Our high-resolution transmission electron microscopy (HRTEM) studies of Sr2TiO4 samples synthesized using various methods have shown that their structure often contains planar defects disturbing the periodicity of layer alternation. This is due to the crystal-chemical features of the R-P layered perovskite-like oxides whose structure is formed by n consecutive layers of perovskite (ABO3)n in alternating with layers of rock-salt type (AO) in various ways along the c crystallographic direction. Planar defects can arise due to a periodicity violation of the layers alternation that also leads to a violation of the synthesized phase stoichiometry. In the present work, a crystallochemical analysis of the possible structure of planar defects is carried out, structures containing defects are modeled, and the effect of such defects on the X-ray diffraction patterns of oxides of the A2BO4 type using Sr2TiO4 is established as an example. For the calculations, we used the method of constructing probabilistic models of one-dimensionally disordered structures. For the first time, the features of diffraction were established, and an approach was demonstrated for determining the concentration of layer alternation defects applicable to layered perovskite-like oxides of the A2BO4 type of any chemical composition. A relation has been established between the concentration of planar defects and the real chemical composition (nonstoichiometry) of the Sr2TiO4 phase. The presence of defects leads to the Ti enrichment of particle volume and, consequently, to the enrichment of the surface with Sr. The latter, in turn, according to the data of a number of authors, can serve as an explanation for the catalytic activity of Sr2TiO4 in the oxidative coupling of methane.

In Situ Study of Reduction of MnxCo3-xO4 Mixed Oxides: The Role of Manganese Content.

A series of Mn-Co mixed oxides with a gradual variation of the Mn/Co molar ratio were prepared by coprecipitation of cobalt and manganese nitrates. The structure, chemistry, and reducibility of the oxides were studied by X-ray diffraction (XRD), X-ray absorption spectroscopy, X-ray photoelectron spectroscopy (XPS), and temperature-programmed reduction (TPR). It was found that at concentrations of Mn below 37 atom %, a solid solution with a cubic spinel structure is formed. At concentrations above 63 atom %, a solid solution is formed on the basis of a tetragonal spinel, while at concentrations in a range of 37-63 atom %, a two-phase system, which contains tetragonal and cubic oxides, is formed. To elucidate the reduction route of mixed oxides, two approaches were used. The first was based on a gradual change in the chemical composition of Mn-Co oxides, illustrating slow changes in the TPR profiles. The second approach consisted in a combination of in situ XRD and pseudo-in situ XPS techniques, which made it possible to directly determine the structure and chemistry of the oxides under reductive conditions. It was shown that the reduction of Mn-Co mixed oxides proceeds via two stages. During the first stage, (Mn, Co)3O4 is reduced to (Mn, Co)O. During the second stage, the solid solution (Mn, Co)O is transformed into metallic cobalt and MnO. The introduction of manganese cations into the structure of cobalt oxide leads to a decrease in the rate of both reduction stages. However, the influence of additional cations on the second reduction stage is more noticeable. This is due to crystallographic peculiarities of the compounds: the conversion from the initial oxide (Mn, Co)3O4 into the intermediate oxide (Mn, Co)O requires only a small displacement of cations, whereas the formation of metallic cobalt from (Mn, Co)O requires a rearrangement of the entire structure.

The Formation of Mn-Ce Oxide Catalysts for CO Oxidation by Oxalate Route: The Role of Manganese Content.

The Mn-Ce oxide catalysts active in the oxidation of CO were studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction (TPR), transition electron microscopy (TEM), energy dispersive X-Ray (EDX), and a differential dissolution technique. The Mn-Ce catalysts were prepared by thermal decomposition of oxalates by varying the Mn:Ce ratio. The nanocrystalline oxides with a fluorite structure and particle sizes of 4-6 nm were formed. The introduction of manganese led to a reduction of the oxide particle size, a decrease in the surface area, and the formation of a MnyCe1-yO2-δ solid solution. An increase in the manganese content resulted in the formation of manganese oxides such as Mn2O3, Mn3O4, and Mn5O8. The catalytic activity as a function of the manganese content had a volcano-like shape. The best catalytic performance was exhibited by the catalyst containing ca. 50 at.% Mn due to the high specific surface area, the formation of the solid solution, and the maximum content of the solid solution.