Dopant activation process in Mg-implanted GaN studied by monoenergetic positron beam.

A process for activating Mg and its relationship with vacancy-type defects in Mg-implanted GaN were studied by positron annihilation spectroscopy. Mg+ ions were implanted with an energy of 10 keV, and the Mg concentration in the subsurface region (≤ 50 nm) was on the order of 1019 cm-3. After the Mg-implantation, N+ ions were implanted to provide a 300-nm-deep box profile with a N concentration of 6 × 1018 cm-3. From capacitance-voltage measurements, the sequential implantation of N was found to enhance the activation of Mg. For N-implanted GaN before annealing, the major defect species were determined to Ga-vacancy related defects such as divacancy. After annealing below 1000 °C, the clustering of vacancies was observed. Above 1200 °C annealing, however, the size of the vacancies started to decrease, which was due to recombinations of vacancy clusters and excess N atoms in the damaged region. The suppression of vacancy clustering by sequential N-implantation in Mg-implanted GaN was attributed to the origin of the enhancement of the Mg activation.

Comparative Analysis of Defects in Mg-Implanted and Mg-Doped GaN Layers on Freestanding GaN Substrates.

Inefficient Mg-induced p-type doping has been remained a major obstacle in the development of GaN-based electronic devices for solid-state lighting and power applications. This study reports comparative structural analysis of defects in GaN layers on freestanding GaN substrates where Mg incorporation is carried out via two approaches: ion implantation and epitaxial doping. Scanning transmission electron microscopy revealed the existence of pyramidal and line defects only in Mg-implanted sample whereas Mg-doped sample did not show presence of these defects which suggests that nature of defects depends upon incorporation method. From secondary ion mass spectrometry, a direct correspondence is observed between Mg concentrations and location and type of these defects. Our investigations suggest that these pyramidal and line defects are Mg-rich species and their formation may lead to reduced free hole densities which is still a major concern for p-GaN-based material and devices. As freestanding GaN substrates offer a platform for realization of p-n junction-based vertical devices, comparative structural investigation of defects originated due to different Mg incorporation processes in GaN layers on such substrates is likely to give more insight towards understanding Mg self-compensation mechanisms and then optimizing Mg doping and/or implantation process for the advancement of GaN-based device technology.

[Kooroo color: 90-day dietary toxicity study in F344 rats].

A subchronic toxicity study on kooroo color was conducted using F344 rats of both genders. Kooroo color is an extract of yam root, Dioscorea matudai Hayata, of which the major components are known to be flavonoid pigments. Use of kooroo as a food color is permitted by the Food Sanitation Law in Japan, but the chronic toxicity has not been evaluated in the literature. Rats were fed the product of kooroo color (PKC) at doses of 0.5%, 1.50%, and 5.0% in basal powder diet, while control groups received PKC-free basal diet, for ninety days. A vehicle control given propylene glycol (PG) alone, at the same dosage that the 5.0% group received, was included, because PKC used in this study contained ca. 80 percent PG, used as an extractant during the manufacturing processes. Daily observation of general behavior, and weekly measurement of body weight as well as food consumption were performed. Hematological, serum biochemical and anatomopathological examinations were conducted at the end of administration. No abnormalities ascribable to the treatment with PKC or PG were noted in any examination in this study. Hence, dietary intake of 5.0% of PKC, i.e., 2,993 mg/kg/day for males, and 3,376 mg/kg/day for females, as a mean daily intake for 90 days, had no observable adverse effect in F344 rats. Therefore, kooroo color has no significant general toxicity, and its toxicity, if any, is of a very low order.

[The basic idea and exercise program of "fall and fracture prevention school" for elderly people].

With the arrival of an aging society in Japan, accidents among elderly people involving falls and bone fractures are on the increase. Efforts to prevent such accidents are strongly required, so the concept of a "fall and fracture prevention school" is spreading. The aims of these classes are to make elderly people aware of the condition of their bodies and to improve deteriorating physical ability through exercise programs, since the latter is the cause of such falls. In conducting an exercise program for the elderly, it is important to make it enjoyable as well as safe.