ABSTRACT
Gelatin is frequently used in various biomedical applications. However, gelatin is generally extracted from an animal source, which can result in issues with reproducibility as well as pathogen transmittance. Therefore, we have investigated the potential of a recombinant peptide based on collagen I (RCPhC1) for tissue engineering applications and more specifically for adipose tissue regeneration. In the current paper, RCPhC1 was functionalized with photo-crosslinkable methacrylamide moieties to enable subsequent UV-induced crosslinking in the presence of a photo-initiator. The resulting biomaterial (RCPhC1-MA) was characterized by evaluating the crosslinking behaviour, the mechanical properties, the gel fraction, the swelling properties and the biocompatibility. The obtained results were compared with the data obtained for methacrylamide-modified gelatin (Gel-MA). The results indicated that the properties of RCPhC1-MA networks are comparable to those of animal-derived Gel-MA. RCPhC1-MA is thus an attractive synthetic alternative for animal-derived Gel-MA and is envisioned to be applicable for a wide range of tissue engineering purposes.
Subject(s)
Biocompatible Materials/chemistry , Collagen/chemistry , Tissue Engineering/methods , HumansABSTRACT
In the present work, gelatin type B is modified with highly reactive norbornene functionalities (Gel-NB) following a one-pot synthesis approach to enable subsequent thiol-ene photo-click crosslinking. The modification strategy displays close control over the amount of introduced functionalities. Additionally, Gel-NB exhibits considerably improved processing capabilities in terms of two-photon polymerization when benchmarked to earlier-reported crosslinkable gelatin derivatives (e.g., gelatin-methacrylamide (Gel-MOD) and gelatin-methacrylamide-aminoethylmethacrylate (Gel-MOD-AEMA)). The improvement is especially apparent in terms of minimally required laser power (20 mW vs ≥60 mW (Gel-MOD) vs ≥40 mW (Gel-MOD-AEMA) at 100 mm s-1 scan speed) and processable concentration range (≥5 w/v% vs ≥10 w/v% (Gel-MOD/Gel-MOD-AEMA)). Furthermore, the proposed functionalization scheme maintains the excellent biocompatibility and cell interactivity of gelatin. Additionally, the norbornene functionalities have potential for straightforward postprocessing "thiol-ene" surface grafting of active molecules. As a consequence, a very promising material toward tissue engineering applications and more specifically, biofabrication, is presented.
Subject(s)
Biocompatible Materials/chemistry , Hydrogels/chemistry , Norbornanes/chemistry , Sulfhydryl Compounds/chemistry , Click Chemistry , Cross-Linking Reagents/chemistry , Gelatin/chemistry , Light , Polyethylene Glycols/chemistry , Polymerization , Tissue EngineeringABSTRACT
Smart pH-responsive superabsorbent polymers (SAPs) could be useful for self-healing of cracks in mortar. They will swell minimally during the alkaline conditions of mixing, leading to only small macro-pores but will swell stronger with a lower pH when water enters the cracks. As such, polysaccharides (alginate, chitosan and agarose) were methacrylated and cross-linked with amine-based monomers (dimethylaminoethyl methacrylate and dimethylaminopropyl methacrylamide) to induce a varying pH-sensitivity. These materials showed a strong cross-linking efficiency and induced moisture uptake capacities up to 122% at 95% relative humidity with a negligible hysteresis. Additionally, interesting pH-responsive swelling capacities were obtained, especially for SAPs based on chitosan and agarose with values up to 110gwater/gSAP. Most of these materials showed limited hydrolysis in cement filtrate solutions, making them very promising for use in mortar.