Local bonding and atomic environments in Ni-catalyzed complex hydrides.

The local bonding and atomic environments in the Ni-catalyzed destabilized system LiBH4/MgH2 and the quaternary borohydride-amide phase Li3BN2H8, were studied by x-ray absorption spectroscopy. In both cases the Ni catalyst was introduced as NiCl2 and a qualitative comparison of the Ni K-edge near-edge structure suggests the Ni2+ is reduced to primarily Ni0 after ball milling. The extended fine structure of the Ni K edge indicates that the Ni is coordinated by approximately 3 boron atoms with an interatomic distance of approximately 2.1 A and approximately 11 Ni atoms in a split shell at around 2.5 and 2.8 A. These results, and the lack of long-range order, suggest that the Ni is present as a disordered nanocluster with a local structure similar to that of Ni3B. In the fully hydrogenated phase of LiBH4/MgH2 a small amount Mg2NiHx was also present. Surface calculations performed using density functional theory suggest that the lowest kinetic barrier for H2 chemisorption occurs on the Ni3B(100) surface.

Pore size distribution and supercritical hydrogen adsorption in activated carbon fibers.

Pore size distributions (PSD) and supercritical H2 isotherms have been measured for two activated carbon fiber (ACF) samples. The surface area and the PSD both depend on the degree of activation to which the ACF has been exposed. The low-surface-area ACF has a narrow PSD centered at 0.5 nm, while the high-surface-area ACF has a broad distribution of pore widths between 0.5 and 2 nm. The H2 adsorption enthalpy in the zero-coverage limit depends on the relative abundance of the smallest pores relative to the larger pores. Measurements of the H2 isosteric adsorption enthalpy indicate the presence of energy heterogeneity in both ACF samples. Additional measurements on a microporous, coconut-derived activated carbon are presented for reference.