ABSTRACT
One of the primary risk factors for implant failure is thought to be implant-related infections during the early healing phase. Developing coatings with cell stimulatory behaviour and bacterial adhesion control is still difficult for bone implants. This study proposes an approach for one-step deposition of biocompatible and antimicrobial Cu-doped TiO2 coatings via glow-discharge sputtering of a mosaic target. During the deposition, the bias of the Ti6Al4V substrates was changed. Structure examination, phase analysis, and surface morphology were carried out using X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray photoelectron spectroscopy (XPS). The hardness values and hydrophilic and corrosion performance were also evaluated together with cytocompatible and antibacterial examinations against E. coli and S. aureus. The results show great chemical and phase control of the bias identifying rutile, anatase, CuO, or ternary oxide phases. It was found that by increasing the substrate bias from 0 to -50 V the Cu content increased from 15.3 up to 20.7 at% while at a high bias of -100 V, the copper content reduced to 3 at%. Simultaneously, apart from the Cu2+ state, Cu1+ is also found in the biased samples. Compared with the bare alloy, the hardness, the water contact angle and corrosion resistance of the biased coatings increased. According to an assessment of in vitro cytocompatibility, all coatings were found to be nontoxic to MG-63 osteoblast cells over the time studied. Copper release and cell-surface interactions generated an antibacterial effect against E. coli and S. aureus strains. The -50 V biased coating combined the most successful results in inhibiting bacterial growth and eliciting the proper responses from osteoblastic cells because of its phase composition, electrochemical stability, hydrophilicity, improved substrate adhesion, and surface roughness. Using this novel surface modification approach, we achieved multifunctionality through controlled copper content and oxide phase composition in the sputtered films.
ABSTRACT
This paper aims to investigate the impact of beam deflection geometry on the structure, surface architecture, and friction coefficient of electron-beam-modified TC4 titanium alloys. During the experiments, the electron beam was deflected in the form of different scanning geometries, namely linear, circular, and matrix. The structure of the treated specimens was investigated in terms of their phase composition by employing X-ray diffraction experiments. The microstructure was studied by scanning electron microscopy (SEM). The surface architecture was examined by atomic force microscopy (AFM). The friction coefficient was studied by a mechanical wear test. It was found that the linear and circular deflection geometries lead to a transformation of the phase composition, from double-phase α + ß to α' martensitic structure. The application of a linear manner of scanning leads to a residual amount of beta phase. The use of a matrix does not tend to structural changes on the surface of the TC4 alloy. In the case of linear geometry, the thickness of the modified zone is more than 800 µm while, in the case of EBSM using circular scanning, the thickness is about 160 µm. The electron-beam surface modification leads to a decrease in the surface roughness to about 27 nm in EBSM with linear deflection geometry and 31 nm in circular deflection geometry, compared to that of the pure TC4 substrate (about 160 nm). The electron-beam surface modification of the TC4 alloy leads to a decrease in the coefficient of friction (COF), with the lowest COF values obtained in the case of linear deflection geometry (0.32). The results obtained in this study show that beam deflection geometry has a significant effect on the surface roughness and friction coefficient of the treated surfaces. It was found that the application of a linear manner of scanning leads to the formation of a surface with the lowest roughness and friction coefficient.