ABSTRACT
Heterogenite is commonly referred in mineralogy literature as a cobalt oxy-hydroxide CoO(OH). However, detailed analysis of Raman and infrared spectra acquired on particularly well-crystallized natural samples of heterogenite suggests that the mineral can be characterized by a delafossite-type structure, with a general chemical formula ABO2. Indeed, the Raman spectrum of heterogenite, along the one with grimaldiite (HCrO2), lacks visible free OH-group vibrational modes, while the infrared spectrum shows strong hydrogen bond absorption bands. HCoO2 is thus a better formulation of heterogenite that describes more clearly its vibrational behavior and avoids the confusion in literature. Electronic backscattered diffraction (EBSD) is then used to distinguish and map the 2H and 3R heterogenite natural polytypes for the first time. The comparison of EBSD and Raman mappings clearly indicates that the 2H polytype is characterized by an additional peak at 1220 cm(-1). The presence/absence is therefore an efficient tool to distinguish both polytypes.
ABSTRACT
Natural heterogenite (CoO·OH) samples were studied by Raman microspectroscopy, electronic microprobe and Electronic BackScattered Diffraction (EBSD). Raw samples and polished sections were made from 10 mines covering the Katanga copperbelt (Katanga Province, Democratic Republic of Congo). Four typical Raman responses have been obtained leading to investigate the laser-induced dehydroxylation of heterogenite into a Co-spinel structure. The results are also compared with EBSD patterns from oven heated heterogenite samples. A close relationship was established between the chemical substitutions of Co by mainly Cu, Ni, Mn and Al and their impact on the mineral Raman response.