Depressed-cladding thulium-doped fiber for applications below 1800 nm.

We present a thulium-doped silica fiber, featuring a depressed cladding, for applications at wavelengths below 1800 nm. The depressed cladding is used as a distributed filter suppressing amplified spontaneous emission at longer wavelengths, which helps promote emission at shorter wavelengths. We describe the fiber design process that was carried out by using a combination of numerical methods. The fiber was prepared in-house by a combination of the standard modified chemical vapor deposition method and nanoparticle doping. We demonstrate the effectiveness and tunability of ASE filtering, which is influenced by fiber bend radius and its variation.

Heat treatment and fiber drawing effect on the luminescence properties of RE-doped optical fibers (RE = Yb, Tm, Ho).

We investigate the influence of various optical fiber fabrication processes on the fluorescence decay of RE ions commonly used in fiber lasers and amplifiers, i.e. Yb3+, Tm3+ and Ho3+. Optical fiber preforms were prepared using the MCVD method combined with Al2O3 nanoparticle doping and subjected to subsequent heat treatment processes such as preform elongation and fiber drawing. The fluorescence decay of RE ions was measured in multiple stages of optical fiber preparation: in an original preform, in an elongated preform (cane), in a standard fiber, and in an overcladded fiber. It was found that heat treatment processing of the preforms generally leads to a faster fluorescence decay, which can be explained by the diffusion of dopants and clustering of RE ions. The fiber drawing exhibited a greater effect compared to preform elongation, which was ascribed to a faster cooling rate of the process. In general, the heat treatment of RE-doped silica glass preforms leads to the decline of fluorescence decay.