ABSTRACT
We report the growth and characterization of uniform-sized nanoparticles of cobalt on n-type silicon (100) substrates by swift heavy ion (SHI) irradiation. The Co thin films of 25-nm thicknesses were grown by e-beam evaporation and irradiated with two different types of ions, 45-MeV Li3+ and 100-MeV O7+ ions with fluences ranging from 1 × 1011 to 1 × 1013 ions/cm2. SHI irradiation, with the beam rastered over the area of the film, resulted in the restructuring of the film into a dense array of Co nanostructures. Surface topography studied by atomic force microscopy revealed narrowed size distributions, with particle sizes ranging from 20 to 50 nm, formed through a self-organized process. Ion fluence-dependent changes in crystallinity of the Co nanostructures were determined by glancing angle X-ray diffraction. Rutherford backscattering spectroscopy analysis showed the absence of beam-induced mixing in this system. Surface restructuring and beam-induced crystallization are the dominant effects, with the nanoparticle size and density being dependent on the ion fluence. Results are analyzed in the context of molecular dynamics calculations of electron-lattice energy transfer.
ABSTRACT
The surface chemistry of GaAs (100) with 50-keV Ar+ ion beam irradiation at off-normal incidence has been investigated in order to elucidate the surface nano-structuring mechanism(s). Core level and valence band studies of the surface composition were carried out as a function of fluences, which varied from 1 × 1017 to 7 × 1017 ions/cm2. Core-level spectra of samples analyzed by X-ray photoelectron spectroscopy confirmed the Ga enrichment of the surface resulting in bigger sized nano-dots. Formation of such nano-dots is attributed to be due to the interplay between preferential sputtering and surface diffusion processes. Valence band measurement shows that the shift in the Fermi edge is higher for Ga- rich, bigger sized nano-dots due to the partial oxide formation of Ga. 'One-dimensional power spectral density' extracted from atomic force micrographs also confirms the significant role of surface diffusion in observed nano-structuring.