Characterization of methacrylated polysaccharides in combination with amine-based monomers for application in mortar.

Smart pH-responsive superabsorbent polymers (SAPs) could be useful for self-healing of cracks in mortar. They will swell minimally during the alkaline conditions of mixing, leading to only small macro-pores but will swell stronger with a lower pH when water enters the cracks. As such, polysaccharides (alginate, chitosan and agarose) were methacrylated and cross-linked with amine-based monomers (dimethylaminoethyl methacrylate and dimethylaminopropyl methacrylamide) to induce a varying pH-sensitivity. These materials showed a strong cross-linking efficiency and induced moisture uptake capacities up to 122% at 95% relative humidity with a negligible hysteresis. Additionally, interesting pH-responsive swelling capacities were obtained, especially for SAPs based on chitosan and agarose with values up to 110gwater/gSAP. Most of these materials showed limited hydrolysis in cement filtrate solutions, making them very promising for use in mortar.

Characterization of methacrylated alginate and acrylic monomers as versatile SAPs.

Superabsorbent polymers (SAPs) based on polysaccharides, especially alginate, could offer a valuable solution in a plethora of applications going from drug delivery to self-healing concrete. This has already been proven with both calcium alginate and methacrylated alginate combined with acrylic acid. In this manuscript, the effect of varying the degree of methacrylation and use of a combination of acrylic acid and acrylamide is investigated to explore the effects on the relevant SAP characteristics. The materials showed high gel fractions and a strong swelling capacity up to 630gwater/gSAP, especially for superabsorbent polymers with a low degree of substitution. The SAPs also showed only a limited hydrolysis in aqueous and cement filtrate solutions.