ABSTRACT
Lignin-based polyol was obtained via oxyalkylation reaction with propylene carbonate using eucalyptus kraft lignin isolated from the industrial cooking liquor by the Lignoboost® procedure. This lignin-based polyol (LBP) was used without purification in the preparation of polyurethane (PU) adhesives combined with polymeric 4,4'-methylenediphenyl diisocyanate (pMDI). A series of adhesives were obtained by varying the NCO/OH ratio of PU counterparts (pMDI and LBPs) and their performance was evaluated by gluing wood pieces under predefined conditions. The adhesion properties of the novel PU adhesive were compared with those of a commercial PU adhesive (CPA). The occurrence and extent of curing reactions and changes in the polymeric network of PA were monitored by Fourier transform infrared spectroscopy (FTIR) and dynamic mechanical analysis. Although the lap shear strength and glass transition temperature of the lignin-based PU adhesives have increased steadily with the NCO/OH ratio ranging from 1.1-2.2, chemical aging resistance can be compromised when the NCO/OH is very low. It was found that the lignin-based PU adhesive with an NCO/OH ratio of 1.3 showed better chemical resistance and adhesion efficiency than CPA possibly because the NCO/OH in the latter is too high as revealed by FTIR spectroscopy. Despite some lower thermal stability and shorter gelation time of lignin-based PU than CPA, the former revealed great potential to reduce the use of petroleum-derived polyols and isocyanates with potential application in the furniture industry as wood bonding adhesive.
ABSTRACT
Currently, the pulp and paper industry generates around 50-70 million tons of lignin annually, which is mainly burned for energy recovery. Lignin, being a natural aromatic polymer rich in functional hydroxyl groups, has been drawing the interest of academia and industry for its valorization, especially for the development of polymeric materials. Among the different types of polymers that can be derived from lignin, polyurethanes (PUs) are amid the most important ones, especially due to their wide range of applications. This review encompasses available technologies to isolate lignin from pulping processes, the main approaches to convert solid lignin into a liquid polyol to produce bio-based polyurethanes, the challenges involving its characterization, and the current technology assessment. Despite the fact that PUs derived from bio-based polyols, such as lignin, are important in contributing to the circular economy, the use of isocyanate is a major environmental hot spot. Therefore, the main strategies that have been used to replace isocyanates to produce non-isocyanate polyurethanes (NIPUs) derived from lignin are also discussed.
ABSTRACT
Oxyalkylation with propylene carbonate (PC) is a safe process to convert lignin into a reactive liquid polyol to be used in polyurethane formulations. In this study, the effect of operating conditions of oxyalkylation (temperature, time and quantify of PC) on the quality of lignin-based polyol in terms hydroxyl number (IOH) and viscosity was studied. Full factorial modeling and response surface methodology (RSM) were applied to study the effect and interaction of process variables on the IOH and viscosity of lignin-based polyols. The results revealed that the IOH is highly affected by the reaction time, while the viscosity is affected by the amount of PC. Validation experiments confirmed the model is reliable. Furthermore, RSM optimization allowed to reduce the amount of PC by about 50% and to increase the lignin content in the polyol from 12.5% to 25% (w/w) depending on the temperature and time of the process and also on the purpose of the polyol produced (i.e., application in rigid foams or adhesives).