Facile Synthesis of Zn-Co-S Nanostrip Cluster Arrays on Ni Foam for High-Performance Hybrid Supercapacitors.

Mixed metal sulfides exhibit outstanding electrochemical performance compared to single metal sulfides and mixed metal oxides because of their richer redox reactions and high electronic conductivity. In the present study, Zn-Co-S nanostrip cluster arrays were formed from ZnCo2O4 grown on Ni foam by an anion exchange reaction using a two-step hydrothermal process. Morphological characterization confirmed that the Zn-Co-S nanostrip cluster arrays had grown homogeneously on the skeleton of the 3D Ni foam. The length of the nanostrip was approximately 8 µm, and the width ranged from 600 to 800 nm. The Ni foam-supported Zn-Co-S nanostrip cluster arrays were assessed directly for electrochemical supercapacitor applications. Compared to ZnCo2O4, the Zn-Co-S electrode exhibited a three-fold higher specific capacity of 830 C g-1 at a specific current of 2.0 A g-1. The higher polarizability, lower electro-negativity, and larger size of the S2- ion played an important role in substituting oxygen with sulfur, which enhanced the performance. The Zn-Co-S//AC hybrid device delivered a maximum specific energy of 19.0 Wh kg-1 at a specific power of 514 W kg-1. The remarkable performance of Zn-Co-S nanostrip cluster arrays highlights their potential as a positive electrode for hybrid supercapacitor applications.

In situ preparation of MgCo2O4 nanosheets on Ni-foam as a binder-free electrode for high performance hybrid supercapacitors.

A binder-free, MgCo2O4 nanosheet-like architecture was prepared on Ni-foam using a hydrothermal method. MgCo2O4/Ni-foam was characterized by X-ray diffraction, field emission scanning electron microscopy (FESEM), and transmission electron microscopy techniques. The FESEM image revealed a nanosheet array-like architecture. The MgCo2O4 nanosheets grown on Ni-foam exhibited the maximum specific capacity of 947 C g-1 at a specific current of 2 A g-1. Approximately 96% of the specific capacity was retained from the maximum specific capacity after 5000 continuous charge-discharge cycles. This hybrid device exhibited a maximum specific capacity of 52 C g-1 at a specific current of 0.5 A g-1, and also exhibited a maximum specific energy of 12.99 W h kg-1 at a specific power of 448.7 W kg-1. These results confirmed that the binder-free MgCo2O4 nanosheets grown on Ni-foam are a suitable positive electrode material for hybrid supercapacitors.

Supercapacitor studies on NiO nanoflakes synthesized through a microwave route.

NiO nanomaterial was synthesized at different calcination temperatures using cetyltrimethyl ammonium bromide (CTAB) as surfactant via microwave method. Thermogravimetric studies revealed the decomposition details of Ni(OH)2 precursor. The structure and morphology of the NiO was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). NiO calcined at 300 °C shows a nanoflake-like structure. A possible formation mechanism has been discussed with time evolution study. Electrochemical studies indicate that the sample calcined at 300 °C exhibits better charge storage. The NiO nanoflakes exhibit maximum specific capacitance of 401 F g(-1) at a current density of 0.5 mA cm(-2). The energy generated and hence the charges collected from wind and solar panels are slow but in many applications the power delivery has to be at a faster rate. Considering this aspect, slow-charge and fast-discharge tests have been performed and reported. The NiO nanoflakes appear to be a promising electrode material for supercapacitor application.