Structural properties and antibacterial effects of hydrophobic and oleophobic sol-gel coatings for cotton fabrics.

In a continuation of previous studies, the wetting properties of the hydrophobic diureapropyltriethoxysilane [bis(aminopropyl)-terminated polydimethylsiloxane (1000)] (PDMSU) sol-gel hybrid, which forms washing-resistant water-repellent finishes on cotton fabrics, were further investigated. The addition of 1H,1H,2H,2H-perfluorooctyltriethoxysilane (PFOTES) to PDMSU resulted in a highly apolar low-energy surface on aluminum with gammaStotal equal to 14.5 mJ/m2 and a DetlaGiwi value of -82 mJ/m2. Mixed PFOTES-PDMSU finishes applied on cotton fabrics increased the water contact angles (thetaw) from approximately 130 degrees (PDMSU) to 147 degrees, also imparting oleophobicity (thetadiiodomethane=130 degrees, thetan-hexadecane=120 degrees) to the finished cotton fabrics. Washing caused breakage of the coating's integrity as established from SEM, which was attributed to the partial removal of PFOTES from the composite films, also shown by subtractive IR attenuated total reflectance (ATR) and XPS spectral measurements made on washed and unwashed fabrics. The antibacterial properties of the PFOTES-PDMSU-finished fabrics were assessed with the transfer method (EN ISO 20743:2007), revealing that the reduction of Escherichia coli bacteria on unwashed cotton fabrics was nearly 100%. Moreover, for washed (10 times) cotton fabrics a much higher bacterial reduction was noted for the PFOTES-PDMSU finishes (60.6+/-10.8%), surpassing PDMSU (30.4+/-6.1%) and commercial fluoroalkoxysilane (FAS) (21.9+/-5.7%) finishes. The structure of PFOTES-PDMSU gels, xerogels, and the corresponding coatings was investigated by analyzing the 29Si NMR and IR ATR spectra and comparing them with the spectra of PFOTES and octameric (T8) PFOTES based polyhedra. The results revealed the tendency of PFOTES to condense in octameric silsesquioxane polyhedra (T8), coexisting in the PDMSU sol-gel network with cyclic tetramers (T4(OH)4) and open cube-like species (T7(OH)3). The presence of -OH-functionalized PFOTES silsesquioxanes, established even in coatings heat-treated at 140 degrees C (15 min), also explained the excellent washing fastness of PFOTES finishes on cotton fabrics. The regenerative nature of the water- and oil-repellent properties of washed PFOTES-PDMSU-finished cotton fabrics was attributed to the surface mobility of the T8 PFOTES based polyhedra, ousted from the coating interior during consecutive washings.

Corrosion studies and interfacial bonding of urea/poly(dimethylsiloxane) sol/gel hydrophobic coatings on AA 2024 aluminum alloy.

Bis[(ureapropyl)triethoxysilane] bis(propyl)-terminated-polydimethylsiloxane 1000 (PDMSU), an organic-inorganic hybrid, diluted in either EtOH or a mixture of EtOH-PrOH, was used in thin film form (<200 nm) to inhibit the corrosion of AA 2024 alloy. Potentiodynamic, time-dependent cyclovoltammetric measurements and salt spray tests showed that the corrosion inhibition of the latter was 10 times higher than that of the former films. This was correlated with the higher degree of hydrolysis and the formation of more open polyhedral silsesquioxane species (T2) in the bulk heat-treated PDMSU/EtOH-PrOH xerogels (29Si NMR spectra). The structure of the coatings deposited on AA 2024 Al alloy was deduced from the infrared reflection-absorption (IR RA) spectra, which revealed more extensive urea-urea interactions and more efficient silane-Al interface bonding for the PDMSU/EtOH-PrOH coatings with higher corrosion inhibition. Ex situ IR RA potentiodynamic spectroelectrochemical measurements of PDMSU coatings revealed that their degradation did not proceed via the formation of silanol groups and consequent hydration of the coatings but that they decomposed above E(corr) by forming fragments composed of -CH2- segments in an all-trans conformation.

Structural and water-repellent properties of a urea/poly(dimethylsiloxane) sol-gel hybrid and its bonding to cotton fabric.

A novel diureapropyltriethoxysilane [bis(aminopropyl)-terminated-poly(dimethylsiloxane) (1000)] (PDMSU) sol-gel hybrid was synthesized and applied on cotton to make it water repellent. Surface-energy values of PDMSU deposited on an aluminum substrate were determined, and the contact angle for water was assessed for impregnated cotton fabrics. The stability of the coatings was determined by repetitive washing, and their degradation was investigated with the help of the infrared attenuated total reflection (ATR) technique. The structure of PDMSU was studied by ATR and 29Si NMR spectroscopy. The results showed the active role of the urea groups in PDMSU/cotton interface bonding, but washing led to the relaxation of the urea-urea associations, as inferred from the appearance of a new amide II band at 1541 cm(-1).