ABSTRACT
The effect of Si addition on the oxidation behaviour of NiCrAlY alloys in the temperature range 950 bis 1100 degrees C has been investigated. During isothermal oxidation oxide growth rates were practically independent of the Si-content. However during cyclic oxidation Si additions were beneficial. Si additions of 1-2(m)/(0) appeared to shift the onset for spallation to longer times. It was found that Si stabilizes the beta-phase and probably it suppresses the formation of metastable Al(2)O(3) modifications.
ABSTRACT
The effect of silicon and titanium on the spallation resistance of alumina scales grown on NiCrAlY-type alloys has been investigated using model alloys with different additions of Si or Ti. For this purpose cyclic oxidation experiments have been carried out at temperatures between 950 and 1100 degrees C. After various times stresses in selected Si-doped samples have been determined by X-ray stress evaluation (XSE) at ambient temperature. The compressive stresses in the scales have been found to increase with an increasing oxidation time tending to become constant for long times. The development of stress is affected by the presence of Si. Laser Raman spectroscopy (LRS) has been calibrated for strain measurement using XSE results. Then LRS has been applied for strain measurement at higher temperatures.