ABSTRACT
Optical thermometry has been widely studied to achieve an inaccessible temperature measurement in submicron scale and it has been reported that the temperature sensitivity depends mainly on host types. In this work, we propose a new method to improve the optical temperature sensitivity of Yb3+-Er3+ co-doped CaWO4 phosphors by doping with Li+, Sr2+, and Mg2+ ions and by controlling excitation powers of 980 nm laser. It is found that the thermometric parameters such as upconversion emission intensity, intensity ratio of green-to-red emission, fluorescence color, emission intensity ratios of thermally coupled levels (2H11/2/4S3/2), and relative and absolute temperature sensitivity can be effectively controlled by doping with Li+, Sr2+, and Mg2+ ions in the Yb3+-Er3+ co-doped CaWO4 system. Moreover, the relative sensitivity SR and the absolute sensitivity SA are proved to be dependent on the pump power of 980 nm laser. The sensitivities of SR and SA in Yb3+-Er3+ co-doped CaWO4 increase about 31.5% and 12%, respectively, by doping with 1 mol% Sr2+.
ABSTRACT
Understanding site-selective fluorescence is one of valuable importance for spectrum modulation. In this Letter, we observed the existence of two non-equivalent Gd-activated crystallographic sites in an Er3+-doped hexagonal Na1.5Gd1.5F6 phosphor. It is proved that two green emissions from the S3/24 level separately originate from the Gd1 (540 nm) and Na2/Gd2 (550-555 nm) crystallographic sites, and the 657 nm red emission from the F9/24 level only originates from Na2/Gd2 site through using the time-resolved luminescence spectra. The 142.2% absolute enhancement of the red emission is realized through the synergistic effect of ultraviolet downconversion and infrared upconversion induced by the 370 nm and 1.54 µm dual-mode excitation.
ABSTRACT
The knowledge of the pump power for which the population of thermally coupled energy levels (TCL) changes with power increase is of valuable importance for optical temperature sensors. In this paper, novel Er3+ doped transparent Sr0.69La0.31F2.31 glass ceramics was fabricated successfully, and its structure is studied by XRD, TEM and HRTEM analyses. The 2H11/2/4S3/2, 4F9/2(1)/4F9/2(2), and 4I9/2(1)/4I9/2(2) levels of Er3+ are proved as TCL by analyzing the temperature dependent fluorescence intensity ratios. The spectrum split, thermal quenching ratio, population stability, and temperature sensitivity from three TCL are observed to be dependent on the pump power. A new fitting method has been developed to establish the relation between fluorescence intensity ratios and temperature. It is found that the combined use of 2H11/2/4S3/2 and 4F9/2(1)/4F9/2(2) as thermally coupled energy levels will get a more precise temperature reading from 62.7 K to 800 K with the help of low excitation power at 66.8 mW/mm2.