Exploitation of thermal gradients for investigation of irradiation temperature effects with charged particles.

The effects of radiation damage on materials are strongly dependant on temperature, making it arguably the most significant parameter of concern in nuclear engineering. Owing to the challenges and expense of irradiating and testing materials, material property data is often limited to few irradiation conditions and material variants. A new technique has been developed which enables the investigation of radiation damage of samples subject to a thermal gradient, whereby a wealth of data over a range of irradiation temperatures is produced from a single irradiation experiment. The results produced are practically inaccessible by use of multiple conventional isothermal irradiations. We present a precipitation-hardened copper alloy (CuCrZr) case-study irradiated with a linear temperature gradient between 125 and 440 °C. Subsequent micro-scale post irradiation characterisation (nanoindentation, transmission electron microscopy and atom probe tomography) highlight the capability to observe mechanical and microstructural changes over a wide range of irradiation temperatures. We observed irradiation-softening in CuCrZr that did not occur due to irradiation-enhanced aging of the Cr-precipitates. Excellent reproducibility of the new technique was demonstrated and replicated irradiation-hardening data from several isothermal neutron irradiation studies. Our new technique provides this data at a fraction of the time and cost required by conventional irradiation experiments.

Ion Microbeam Analyses of Dust Particles and Codeposits from JET with the ITER-Like Wall.

Generation of metal dust in the JET tokamak with the ITER-like wall (ILW) is a topic of vital interest to next-step fusion devices because of safety issues with plasma operation. Simultaneous Nuclear Reaction Analysis (NRA) and Particle-Induced X-ray Emission (PIXE) with a focused four MeV 3He microbeam was used to determine the composition of dust particles related to the JET operation with the ILW. The focus was on "Be-rich particles" collected from the deposition zone on the inner divertor tile. The particles found are composed of a mix of codeposited species up to 120 µm in size with a thickness of 30-40 µm. The main constituents are D from the fusion fuel, Be and W from the main plasma-facing components, and Ni and Cr from the Inconel grills of the antennas for auxiliary plasma heating. Elemental concentrations were estimated by iterative NRA-PIXE analysis. Two types of dust particles were found: (i) larger Be-rich particles with Be concentrations above 90 at% with a deuterium presence of up to 3.4 at% and containing Ni (1-3 at%), Cr (0.4-0.8 at%), W (0.2-0.9 at%), Fe (0.3-0.6 at%), and Cu and Ti in lower concentrations and (ii) small particles rich in Al and/or Si that were in some cases accompanied by other elements, such as Fe, Cu, or Ti or W and Mo.