ABSTRACT
Polyurethane (PU) coatings are often applied on high added value technical textiles. Key factor to success of PU coatings is its versatility and durability. Up to today most PU textile coatings are solvent-based or water-based. Recent advances are made in applying bio-based PU on textiles. Currently, polymers made from renewable raw materials are experiencing a renaissance, owing to the trend to reduce CO2 emissions, the switch to CO2-neutral renewable products and the depletion of fossil resources. However, the application of bio-based coatings on textiles is limited. The present paper discusses the potential of a bio-based anionic PU dispersion as an environment friendly alternative for petroleum-based PU in textile coating. Coatings were applied on textile via knife over roll. The chemical, thermal and mechanical properties of the bio-based PU coating were characterised via FT-IR, thermogravimetric analysis, differential scanning calorimetry and tensile test. The performance of the coating was studied by evaluating antimicrobial properties, fire retardancy, the resistance to hydrostatic pressure initially and after washing, QUV ageing and hydrolysis test. The developed bio-based PUD coating complied to the fire retardancy test ISO 15025 and exhibited excellent hydrostatic pressure, QUV ageing resistance, hydrolysis resistance, wash fastness at 40 °C.
ABSTRACT
Flame retardancy is often required in various textile applications. Halogenated flame retardants (FR) are commonly used since they have good FR performance. Several of these components are listed under REACH. Halogen-free FR compounds have been developed as alternatives. So far, not many biobased FR have made it to the market and are being applied in the textile sector, leaving great opportunities since biobased products are experiencing a renaissance. In this study, renewable FR based on sorbitol and isosorbide were synthesised. The reaction was performed in the melt. The resulting biobased FR were characterised via FT-IR, thermogravimetric analysis (TGA) and X-ray fluorescence (XRF). Cotton fabrics functionalized with the developed biobased FR passed ISO 15025 FR test. After washing, the FR properties of the fabrics decreased (longer afterflame and afterglow time) but still complied with ISO 15025, indicating the biobased FR were semi-permanent. The amount of residue of modified sorbitol and isosorbide measured at 600 °C in air was 31% and 27%, respectively. Cotton treated with biobased modified FR showed no ignition during cone calorimetry experiments, indicating a flame retardancy. Furthermore, a charring of the FR containing samples was observed by means of cone calorimetry and TGA measurements.
ABSTRACT
Asymmetric Fe-Mn oxide hybrid nanoparticles have been obtained by a seed-mediated thermal decomposition-based synthesis route. The use of benzyl ether as the solvent was found to promote the orientational growth of Mn1-xO onto the iron oxide nanocube seeds yielding mainly dimers and trimers whereas 1-octadecene yields large nanoparticles. HRTEM imaging and HAADF-STEM tomography performed on dimers show that the growth of Mn1-xO occurs preferentially along the edges of iron oxide nanocubes where both oxides share a common crystallographic orientation. Fourier filtering and geometric phase analysis of dimers reveal a lattice mismatch of 5% and a large interfacial strain together with a significant concentration of defects. The saturation magnetization is lower and the coercivity is higher for the Fe-Mn oxide hybrid nanoparticles compared to the iron oxide nanocube seeds.
