Rear textured p-type high temperature passivating contacts and their implementation in perovskite/silicon tandem cells.

Silicon solar cells based on high temperature passivating contacts are becoming mainstream in the photovoltaic industry. Here, we developed a high-quality boron-doped poly-silicon hole contact. When combined with a co-processed phosphorus-doped poly-silicon electron contact, high-voltage silicon bottom cells could be demonstrated and included in 28.25%-efficient perovskite/Si tandems. The active area was 4 cm2 active area and the front electrode was screen-printed.

Understanding and Mitigating the Degradation of Perovskite Solar Cells Based on a Nickel Oxide Hole Transport Material during Damp Heat Testing.

The development of stable materials, processable on a large area, is a prerequisite for perovskite industrialization. Beyond the perovskite absorber itself, this should also guide the development of all other layers in the solar cell. In this regard, the use of NiOx as a hole transport material (HTM) offers several advantages, as it can be deposited with high throughput on large areas and on flat or textured surfaces via sputtering, a well-established industrial method. However, NiOx may trigger the degradation of perovskite solar cells (PSCs) when exposed to environmental stressors. Already after 100 h of damp heat stressing, a strong fill factor (FF) loss appears in conjunction with a characteristic S-shaped J-V curve. By performing a wide range of analysis on cells and materials, completed by device simulation, the cause of the degradation is pinpointed and mitigation strategies are proposed. When NiOx is heated in an air-tight environment, its free charge carrier density drops, resulting in a band misalignment at the NiOx/perovskite interface and in the formation of a barrier impeding hole extraction. Adding an organic layer between the NiOx and the perovskite enables higher performances but not long-term thermal stability, for which reducing the NiOx thickness is necessary.

Efficient Monolithic Perovskite/Silicon Tandem Solar Cell with Cell Area >1 cm(2).

Monolithic perovskite/crystalline silicon tandem solar cells hold great promise for further performance improvement of well-established silicon photovoltaics; however, monolithic tandem integration is challenging, evidenced by the modest performances and small-area devices reported so far. Here we present first a low-temperature process for semitransparent perovskite solar cells, yielding efficiencies of up to 14.5%. Then, we implement this process to fabricate monolithic perovskite/silicon heterojunction tandem solar cells yielding efficiencies of up to 21.2 and 19.2% for cell areas of 0.17 and 1.22 cm(2), respectively. Both efficiencies are well above those of the involved subcells. These single-junction perovskite and tandem solar cells are hysteresis-free and demonstrate steady performance under maximum power point tracking for several minutes. Finally, we present the effects of varying the intermediate recombination layer and hole transport layer thicknesses on tandem cell photocurrent generation, experimentally and by transfer matrix simulations.