ABSTRACT
Herein, micron-sized silver particles were prepared using the chemical reduction method by employing a Y-type microjet reactor, silver nitrate as the precursor, ascorbic acid as the reducing agent, and gelatin as the dispersion at room temperature (23 °C ± 2°C). Using a microjet reactor, the two reaction solutions collide and combine outside the reactor, thereby avoiding microchannel obstruction issues and facilitating a quicker and more convenient synthesis process. This study examined the effect of the jet flow rate and dispersion addition on the morphology and size of silver powder particles. Based on the results of this study, spherical and dendritic silver particles with a rough surface can be prepared by adjusting the flow rate of the reaction solution and gelatin concentration. The microjet flow rate of 75 mL/min and the injected gelatin amount of 1% of the silver nitrate mass produced spherical ultrafine silver particles with a size of 4.84 µm and a tap density of 5.22 g/cm3.
ABSTRACT
In this paper, micro-size spherical silver particles were prepared by using a wet-chemical reduction method. The silver particles were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and a laser particle-size analyzer. The results indicate that different types and the content of surfactants can be used to prevent the accumulation, and control the morphology and particle size distribution, of silver particles. Moreover, the morphology of silver particles was changed from polyhedral to spherical when the pH was raised from 1 to 3. Under the optimal synthesis conditions (0.1 mol/L silver nitrate, 0.06 mol/L ascorbic acid, gelatin (5% by weight of silver nitrate), pH = 1), the micro-size spherical silver particles with diameter of 5-8 µm were obtained. In addition, the resistivity of conductive silver paste that prepared with the as-synthesized spherical silver particles was discussed in detail and the average resistivity of the conductive silver paste was 3.57 × 10-5 Ω·cm after sintering at 140 °C for 30 min.
ABSTRACT
Extrahepatic metastasis confers unfavorable patient prognosis in patients with hepatocellular carcinoma (HCC), however, reliable markers allowing prediction of extrahepatic metastasis at the time of initial diagnosis are still lacking. This study was to identify gene-level copy number aberrations (CNAs) related to extrahepatic metastasis-free survival of HCC patients, and further examine the associations between CNAs and gene expression. Array comparative genomic hybridization (aCGH) and expression array were used to analyze gene CNAs and expression levels, respectively. The associations between CNAs of a panel of 20 genes and extrahepatic metastasis-free survival were analyzed in 66 patients with follow-up period of 1.6-90.5 months. The gene expression levels between HCCs with and without gene CNA were compared in 109 patients with HCC. We observed that gains at MDM4 and BCL2L1, and losses at APC and FBXW7 were independent prognostic markers for extrahepatic metastasis-free survival of HCC patients. Integration analysis of aCGH and expression data showed that MDM4 and BCL2L1 were significantly upregulated in HCCs with gene gain, while APC and FBXW7 were significantly downregulated in HCCs with gene loss. We concluded that gene gains at MDM4 and BCL2L1, and losses at APC and FBXW7, with concordant expression changes, were associated with extrahepatic metastasis-free survival of HCC patients and have potential to act as novel prognostic markers.