ABSTRACT
A magnetically tunable magnetoelectric transducer consisting of rectangular Fe82Ga18(FeGa)/Pb(Zr,Ti)O3(PZT) composites is developed, and their magnetoimpedance and magnetocapacitance effects are investigated under bending and longitudinal modes. Specifically, the composites' impedance and capacitance are found to vary with dc magnetic field Hdc, which results from the varied effective dielectric permittivity of the FeGa/PZT composite with Hdc due to the delta E effect, magnetostrictive effect of FeGa and mechanism responsible for ME coupling between the FeGa and PZT layers. Furthermore, the FeGa/PZT bilayered composite exhibits both bending and longitudinal vibration modes due to the asymmetrical stress distributions. The maximum ΔZ/Z of the FeGa/PZT composite is about 215% at the antiresonance frequency fa = 28.78 kHz of the bending-mode, which is 2.53 times as high as that at the antiresonance frequency fa = 107.9 kHz of the longitudinal mode, while the maximum ΔC/C of the FeGa/PZT composite is about 406% at the resonance frequency fr = 28.5 kHz of the bending mode, which is 3.5 times as high as that at the antiresonance frequency fa = 106.6 kHz of the longitudinal mode. This study plays a guiding role for the design and corresponding application of magnetic sensors, magnetic-field-tuned electronic devices and multiple frequency ultrasonic transducers.
ABSTRACT
The rectangular magnetoelectric (ME) composites of Metglas/PZT and Terfenol-D/PZT are prepared, and the effects of a magnetostrictive layer's material characteristics on the magnetoimpedance of ME composite are discussed and experimentally investigated. The theoretical analyses show that the impedance is not only dependent on Young's modulus and the magnetostrictive strain of magnetostrictive material but is also influenced by its relative permeability. Compared with Terfenol-D, Metglas possesses significantly higher magnetic permeability and larger magnetostrictive strain at quite low Hdc due to the small saturation field, resulting in the larger magnetoimpedance ratio. The experimental results demonstrate that the maximum magnetoimpedance ratios (i.e., ΔZ/Z) of Metglas/PZT composite are about 605.24% and 239.98% at the antiresonance and resonance, respectively. Specifically, the maximum ΔZ/Z of Metglas/PZT is 8.6 times as high as that of Terfenol-D/PZT at the antiresonance. Such results provide the fundamental guidance in the design and fabrication of novel multifunction devices based on the magnetoimpedance effect of ME composites.