ABSTRACT
Natural clinoptilolite tuff (CL) and chabazite-clinoptilolite tuff (CH) were modified in fixed-bed column by immobilization of hexadecyltrimethylammonium bromide (HDTMA-Br), then investigated as a sorbent for inorganic anions of Cr(VI). The proposed modification technique combined with surfactant solution batching allows minimizing the surfactant loses through foaming and crystallization and creation of stable organic coverage. The HDTMA loading depended on the mineral composition of the zeolitic tuff, the topology of its external surface, and process conditions. The maximum surface coverage was obtained by gradually dosing surfactant solution in the smallest volume of batches and corresponded up to 100% and 182% of external cation exchange capacity (ECEC) for mono and double layer coverage, respectively. In case of mono layer coverage, modification proceeds until the exhaustion of surfactant in supply solution, while in the double layer one, until equilibrium of HDTMA concentration in both zeolitic and liquid phases was established. The efficiency of Cr(VI) uptake by prepared surface modified zeolites (SMZs) increased with increasing of HDTMA loading. In the case of mono layer SMZs, the capacities of CH-HDTMA and CL-HDTMA were 10.3 and 5.4 mg/g, respectively, while in the case of double layer SMZs, the amount of Cr uptake on CH-HDTMA and CL-HDTMA were 16.8 and 15 mg/g, respectively. Ion exchange is the predominant mechanism of Cr(VI) sorption but it takes place only if modification resulted in at least partial double layer coverage. The XPS analysis reveals Cr(VI) reduction to a less-toxic Cr(III) by the electron donating N-containing groups and by reaction with Fe+2 ions on the zeolite external surface.
ABSTRACT
Recently, two-dimensional transition metal dichalcogenides (TMDs) have received tremendous attention in many fields including environmental remediation. Magnetic nanoparticles (Fe3O4NPs) decorated with MoS2 (MoS2@Fe3O4NPs) have been synthesized via a new one-step synthesis route and utilized as an efficient adsorbent for removal of Cr(VI)/Cr(III) from aqueous solutions. The obtained MoS2@Fe3O4NPs with numerous surface hydroxyl groups show uniform size and shape, excellent water-dispersibility, and superior magnetic property to enhance the adsorption. The physicochemical properties of the adsorbent prior to and after adsorption of Cr(VI)/Cr(III) were extensively characterized using several advanced instrumental techniques.The adsorption of Cr(VI)/Cr(III) on MoS2@Fe3O4NPs was performed under batch conditions aiming at identification of optimal contact time, pH value of chromium solution, and influence of the presence of competitive ions. This study was supported by modeling of adsorption equilibrium and kinetics by using empirical equations.