3D direct laser writing of microstructured optical fiber tapers on single-mode fibers for mode-field conversion.

We present a design and fabrication approach for 3D printed polymer microstructured optical fiber tapers on standard single-mode glass fibers for efficient and compact mode-field conversion. This paves the way towards complex functionalized fiber tips for various applications, like sensors and beam shaping components, currently limited by the mode-field size and distribution of standard optical fibers. In this paper, we demonstrate the potential of mode-field converting tapers for relaxing the misalignment tolerance in fiber-to-fiber connections and maximizing the coupling efficiency in fiber-to-chip connections. We demonstrate a mode-field diameter expansion ratio of 1.7 and reduction ratio of 3 and show that our microstructured tapers achieve a comparable performance in coupling efficiency as their step-index counterparts, while providing greater robustness.

Vertical liquid controlled adiabatic waveguide coupler.

A broadband vertical liquid controlled optical waveguide coupler (LCC) is demonstrated. The fabricated vertical LCC with silicon nitride (SiN) waveguides can switch light between 2 stacked photonic circuit layers with zero energy consumption in a steady switch state. In combination with low-loss interlayer waveguide crossovers they enable large scale non-volatile switch circuits with low loss. The fabricated vertical LCC has a loss less than 2.0 dB in bar state and less than 2.6 dB in cross state over the telecommunication wavelength range 1260 nm to 1630 nm. Interlayer waveguide crossovers with the same interlayer oxide thickness as the LCC have a loss less than 0.06 dB over the same wavelength range. The crosstalk of the LCC is less than -21 dB over the wavelength range 1500 nm to 1630 nm for both bar and cross state.

Oil-in-water emulsion impregnated electrospun poly(ethylene terephthalate) fiber mat as a novel tool for optical fiber cleaning.

HYPOTHESIS: The complete removal of remaining polymer debris after stripping of optical fiber cables is essential for high precision connection between two fibers. It can be anticipated that electrospun porous membranes as cleaning wipes are able to trap and retain polymer debris within their pores. Impregnation of an oil-in-water emulsion as cleaning agent lowers the interfacial tension between debris and the optical fiber thereby enabling the straightforward removal of polymer debris from the optical fiber. EXPERIMENTS: Electrospun membranes of poly(ethylene terephthalate) (PET) and cellulose acetate (CA) were obtained with fiber diameters of 0.430 µm and 2 µm respectively. The oil-in-water emulsion was formulated with 10 wt% medium chain triglyceride (MCT) and 10 wt% Tween 80 surfactant in an aqueous phosphate buffer solution. FINDINGS: In a scoring range from 0 to 5 for which the score 0 indicated superior cleaning and the score 5 referred to the least efficient cleaning, the electrospun fiber mats (without emulsion) scored within the range of 2-4 while emulsion impregnated electrospun fiber mats revealed the best score of 0. A drastic improvement was thus clearly evident from the obtained results when the cleaning emulsion was applied. The materials developed herein thus represent a new class of soft cleaning agents for optical fibers.

Design and tolerance analysis of a low bending loss hole-assisted fiber using statistical design methodology.

We present the design of a low bending loss hole-assisted fiber for a 180?-bend fiber socket application, including a tolerance analysis for manufacturability. To this aim, we make use of statistical design methodology, combined with a fully vectorial mode solver. Two resulting designs are presented and their performance in terms of bending loss, coupling loss to Corning SMF-28 standard telecom fiber, and cut-off wavelength is calculated.