Marginal integrity in minimally invasive molar resin composite restorations: Impact of polymerization shrinkage.

OBJECTIVES: This study utilized non-linear finite element (FE) models to explore polymerization shrinkage and its impact on marginal integrity in molars following both selective caries removal (SCR) and conventional treatment. Specifically, we performed 2D in silico simulations to study residual stresses post-resin polymerization shrinkage and their influence on the marginal integrity of various restoration types. METHODS: Initially, FE models were developed based on a cohesive zone framework to simulate crack propagation along the bonded interfaces between restoration and tooth structure in SCR-treated molars with class I and class II restorations. The modeled resin composite restorations first underwent polymerization shrinkage and were then subjected to various occlusal loading conditions. Stress magnitudes and distributions were identified to evaluate the margin integrity and predict the mechanism and location of interfacial failure. RESULTS AND DISCUSSION: The FE models computed polymerization shrinkage stresses of less than 1 MPa, exerting a minor influence on the composite/tooth interface. Occlusal loading, however, significantly impacted the load-bearing capacity of the composite/tooth (c/t) interface, potentially jeopardizing the restoration integrity. Especially under bi-axial occlusal loading, interfacial debonding occurred in the vertical cavity walls of the class I restorations, increasing the risk of failure. Notably, SCR-treated teeth exhibited better margin integrity than restored teeth after complete caries removal (NCR). These findings provide valuable insights into the mechanical behavior of SCR-treated teeth under different loading conditions and highlight the importance of considering the load scenarios that may lead to failure at the c/t interface. By investigating the factors influencing crack initiation and delamination, this novel research contributes to the optimization of restorative treatments and aids in the design of more resilient dental restorations.

Substantial regional differences in the biomechanical behavior of molar treated with selective caries tissue removal technique: a finite element study.

OBJECTIVES: Selective caries removal (SCR) is recommended over non-selective removal for managing deep carious lesions to avoid pulp exposure and maintain pulp vitality. During SCR, residual carious dentin is left behind and sealed beneath the restoration. The biomechanical effects of such residual lesions on the restored tooth remain unclear and were assessed using finite element modeling (FEM). METHODS: Based on µ-CT images of a healthy permanent human third molar, we developed five finite element models. Generic class I and II cavity restorations were modeled where residual lesions of variable sizes were either left or fully removed on occlusal and proximal surfaces. The cavities were restored with adhesive composite. All 3D-FE models were compared with a model of a healthy, non-treated molar. A vertical load of 100 N was applied onto the occlusal surface. RESULTS: Regardless of the lesion size, in molars with occlusal lesions higher mean stresses were predicted along the filling-lesion interface than in all other models. The smallest occlusal lesion (Ø1 = 1 mm) resulted in the highest maximum stresses at the filling-lesion interface with large stress concentrations at the filling walls indicating failure risk. In conclusion, lesion site and extent are influencing parameters affecting the filling-lesion interactions and thus the biomechanical behavior of the tooth after SCR. SIGNIFICANCE: Retaining carious lesions around the pulpal floor affects the deformation and stress states in tooth-filling complexes. The higher stresses observed in molars with occlusal lesions may affect restoration stability and longevity. Suprisingly, more extended occlusal lesions may provide a more favorable tooth performance than less extended ones. In contrast, in molars with proximal lesions the residual lesion had only limited effect on the tooth's biomechanical condition.