ABSTRACT
In the present study, we propose a hybrid manufacturing route to produce high-quality Ti6Al4V parts, combining additive powder laser directed energy deposition (L-DED) for manufacturing of preforms, with subsequent hot forging as a thermomechanical processing (TMP) step. After L-DED, the material was hot formed at two different temperatures (930 °C and 1070 °C) and subsequently heat-treated for stress relief annealing. Tensile tests were performed on small sub-samples, taking into account different sample orientations with respect to the L-DED build direction and resulting in very good tensile strengths and ductility properties, similar or superior to the forged material. The resulting microstructure consists of very fine grained, partially globularized alpha grains, with a mean diameter ~0.8-2.3 µm, within a beta phase matrix, constituting between 2 and 9% of the sample. After forging in the sub-beta transus temperature range, the typical L-DED microstructure was no longer discernible and the anisotropy in tensile properties, common in additive manufacturing (AM), was significantly reduced. However, forging in the super-beta transus temperature range resulted in remaining anisotropies in the mechanical properties as well as an inferior tensile strength and ductility of the material. It was shown, that by combining L-DED with thermomechanical processing in the sub-beta transus temperature range of Ti6Al4V, a suitable microstructure and desirable mechanical properties for many applications can be obtained, with the advantage of reducing the material waste.
ABSTRACT
While repair is mainly used to restore the original part geometry and properties, hybrid manufacturing aims to exploit the benefits of each respective manufacturing process regarding either processing itself or resulting part characteristics. Especially with the current implementation of additive manufacturing in the production of TiAl, turbine blades for both hybrid manufacturing and repair new opportunities are enabled. One main issue is the compatibility of the two or more material types involved, which either differ regarding composition or microstructure or both. In this study, a TNMTM-alloy (Ti-Nb-Mo) was manufactured by different processes (casting, forging, laser additive manufacturing) and identically heat-treated at 1290 °C. Chemical compositions, especially aluminum and oxygen contents, were measured, and the resulting microstructures were analyzed with Scanning Electron Microscopy (SEM) and High-energy X-ray diffraction (HEXRD). The properties were determined by hardness measurements and high-temperature compression tests. The comparison led to an overall assessment of the theoretical compatibility. Experiments to combine several processes were performed to evaluate the practical feasibility. Despite obvious differences in the final phase distribution caused by deviations in the chemical composition, the measured properties of the samples did not differ significantly. The feasibility of combining direct energy deposition (DED) with either casting or laser powder bed fusion (LPBF) was demonstrated by the successful build of the dense, crack-free hybrid material.
ABSTRACT
Laser additive manufacturing is attractive for the production of complex, three-dimensional parts from metallic powder using a computer-aided design model1-3. The approach enables the digital control of the processing parameters and thus the resulting alloy's microstructure, for example, by using high cooling rates and cyclic re-heating4-10. We recently showed that this cyclic re-heating, the so-called intrinsic heat treatment, can trigger nickel-aluminium precipitation in an iron-nickel-aluminium alloy in situ during laser additive manufacturing9. Here we report a Fe19Ni5Ti (weight per cent) steel tailor-designed for laser additive manufacturing. This steel is hardened in situ by nickel-titanium nanoprecipitation, and martensite is also formed in situ, starting at a readily accessible temperature of 200 degrees Celsius. Local control of both the nanoprecipitation and the martensitic transformation during the fabrication leads to complex microstructure hierarchies across multiple length scales, from approximately 100-micrometre-thick layers down to nanoscale precipitates. Inspired by ancient Damascus steels11-14-which have hard and soft layers, originally introduced via the folding and forging techniques of skilled blacksmiths-we produced a material consisting of alternating soft and hard layers. Our material has a tensile strength of 1,300 megapascals and 10 per cent elongation, showing superior mechanical properties to those of ancient Damascus steel12. The principles of in situ precipitation strengthening and local microstructure control used here can be applied to a wide range of precipitation-hardened alloys and different additive manufacturing processes.
ABSTRACT
Maraging steels are used to produce tools by Additive Manufacturing (AM) methods such as Laser Metal Deposition (LMD) and Selective Laser Melting (SLM). Although it is well established that dense parts can be produced by AM, the influence of the AM process on the microstructure-in particular the content of retained and reversed austenite as well as the nanostructure, especially the precipitate density and chemistry, are not yet explored. Here, we study these features using microhardness measurements, Optical Microscopy, Electron Backscatter Diffraction (EBSD), Energy Dispersive Spectroscopy (EDS), and Atom Probe Tomography (APT) in the as-produced state and during ageing heat treatment. We find that due to microsegregation, retained austenite exists in the as-LMD- and as-SLM-produced states but not in the conventionally-produced material. The hardness in the as-LMD-produced state is higher than in the conventionally and SLM-produced materials, however, not in the uppermost layers. By APT, it is confirmed that this is due to early stages of precipitation induced by the cyclic re-heating upon further deposition-i.e., the intrinsic heat treatment associated with LMD. In the peak-aged state, which is reached after a similar time in all materials, the hardness of SLM- and LMD-produced material is slightly lower than in conventionally-produced material due to the presence of retained austenite and reversed austenite formed during ageing.