Driving electrochemical corrosion of implanted CoCrMo metal via oscillatory electric fields without mechanical wear.

Decades of research have been dedicated to understanding the corrosion mechanisms of metal based implanted prosthetics utilized in modern surgical procedures. Focused primarily on mechanically driven wear, current fretting and crevice corrosion investigations have yet to precisely replicate the complex chemical composition of corrosion products recovered from patients' periprosthetic tissue. This work specifically targets the creation of corrosion products at the metal on metal junction utilized in modular hip prosthetics. Moreover, this manuscript serves as an initial investigation into the potential interaction between implanted CoCrMo metal alloy and low amplitude electrical oscillation, similar in magnitude to those which may develop from ambient electromagnetic radiation. It is believed that introduction of such an electrical oscillation may be able to initiate electrochemical reactions between the metal and surrounding fluid, forming the precursor to secondary wear particles, without mechanically eroding the metal's natural passivation layer. Here, we show that a low magnitude electrical oscillation (≤ 200 mV) in the megahertz frequency (106 Hz) range is capable of initiating corrosion on implanted CoCrMo without the addition of mechanical wear. Specifically, a 50 MHz, 200 mVpp sine wave generates corrosion products comprising of Cr, P, Ca, O, and C, which is consistent with previous literature on the analysis of failed hip prosthetics. These findings demonstrate that mechanical wear may not be required to initiate the production of chemically complex corrosion products.

Investigation of the effects of electrochemical reactions on complex metal tribocorrosion within the human body.

Although total hip arthroplasty (THA) is considered to be the most successful orthopedic operation in restoring mobility and relieving pain, common Metal-on-Metal (MoM) implants developed in the past decade suffer from severe inflammatory reactions of the surrounding tissue caused by the premature corrosion and degradation of the implant. A substantial amount of research has been dedicated to the investigation of mechanically driven fretting and crevice corrosion as the primary mechanism of implant failure. However, the exact mechanism by which hip implant breakdown occurs remains unknown, as current in vitro fretting and crevice corrosion studies have failed to completely replicate the corrosion characteristics of recovered implants. Here, we show that minor electric potential oscillations on a model hip implant replicate the corrosion of failed implants without the introduction of mechanical wear. We found in a controlled lab setting that small electrical oscillations, of similar frequency and magnitude as those resulting from ambient electromagnetic waves interacting with the metal of the implant, can force electrochemical reactions within a simulated synovial fluid environment that have not been previously predicted. In lab testing we have shown the replication of titanium, phosphorous, and oxygen deposition onto the surface of ASTM astm:F75 CoCrMo metal alloy test specimens, matching the chemical composition of previously retrieved wear particles from failed patient prosthetics. Our results demonstrate that the electrical activity and ensuing electrochemical activity excites two corrosion failure modes: direct dissolution of the medically implantable alloy, leaching metal ions into the body, and surface deposition growth, forming the precursor of secondary wear particles. We anticipate our findings to be the foundation for the future development and testing of electrochemically resistant implantable material.

Novel investigation of perovskite membrane based electrochemical nitric oxide control phenomenon.

The combustion of hydrocarbon fuels within the automotive industry results in harmful and reactive incomplete combustion byproducts. Specifically, nitric oxide emissions (NO) lead to increased smog, acid rain, climate change, and respiratory inflammation within the population [Nitrogen Dioxide | American Lung Association]. Current methods for treating combustion exhaust include the catalytic converter in conjunction with nitrogen oxide traps. However, there is no active, continuous reduction method that does not require restrictions on the combustion environment (Hirata in Catal Surv Asia 18:128-133, 2014). Here, a small voltage potential oscillation across a newly designed electro-chemical catalytic membrane significantly reduces NO emissions. A ceramic membrane consisting of two dissimilar metal electrodes, sandwiching a dielectric layer, is able to achieve an NO reduction in excess of 2X that of a platinum group metal (PGM) three way catalytic converter. An analysis of the exhaust effluent from the membranes indicates N2O as a precursor to N2 and O2 formation, without the introduction of ammonia (NH3), during the reaction of NO indicating a divergence from current literature. Our results demonstrate how an oscillatory electric potential on a catalytic surface may alter anticipated reaction chemistry and interaction between the catalytic surface and fluid flow.