Ion-Exchange Loading Promoted Stability of Platinum Catalysts Supported on Layered Protonated Titanate-Derived Titania Nanoarrays.

Supported metal catalysts are one of the major classes of heterogeneous catalysts, which demand good stability in both the supports and catalysts. Herein, layered protonated titanate-derived TiO2 (LPT-TiO2) nanowire arrays were synthesized to support platinum catalysts using different loading processes. The Pt ion-exchange loading on pristine LPTs followed by thermal annealing resulted in superior Pt catalysts supported on the LPT-TiO2 nanoarrays with excellent hydrothermal stability and catalytic performance toward CO and NO oxidations as compared to the Pt catalysts through wet-impregnation on the anatase TiO2 (ANT-TiO2) nanoarrays resulted from thermal annealing of LPT nanoarrays. Both loading processes resulted in highly dispersed Pt nanoparticles (NPs) with average sizes smaller than 1 nm at their pristine states. However, after hydrothermal aging at 800 °C for 50 h, highly dispersed Pt NPs were only retained on the ion-exchanged LPT-TiO2 nanoarrays with the support structure consisting of a mixture of 74% anatase and 26% rutile TiO2. For the wet-impregnation loading directly on anatase TiO2 nanoarrays derived from LPT, the Pt catalysts experienced severe agglomeration after hydrothermal aging, with the nanoarray supports consisting of 86% anatase and 14% rutile TiO2. Spectroscopy analysis suggested that Pt2+ cations intercalated into the interlayers of the titanate frameworks through ion-exchange impregnation procedure, which altered the chemical and electronic structures of the catalysts, resulting in the shifts of the electronic binding energy, Raman bands, and optical energy bandgap. The ion-exchangeable nature of LPT nanoarrays clearly provides a structural modification in Pt-doped LPT that has resulted in a strong interaction between the Pt catalysts and LPT-TiO2 nanoarray supports, leading to the enhanced hydrothermal stability of the catalysts. Considering the wide applications of the LPT and TiO2 nanomaterials as supports for catalysts, this finding provides a new pathway to design highly stable supported metal catalysts for different reactions.

Pyrolytic decomposition of ammonia borane to boron nitride.

The thermal decomposition of ammonia borane was studied using a variety of methods to qualitatively identify gas and remnant solid phase species after thermal treatments up to 1500 °C. At about 110 °C, ammonia borane begins to decompose yielding H(2) as the major gas phase product. A two step decomposition process leading to a polymeric -[NH═BH](n)- species above 130 °C is generally accepted. In this comprehensive study of decomposition pathways, we confirm the first two decomposition steps and identify a third process initiating at 1170 °C which leads to a semicrystalline hexagonal phase boron nitride. Thermogravimetric analysis (TGA) was used to identify the onset of the third step. Temperature programmed desorption-mass spectroscopy (TPD-MS) and vacuum line methods identify molecular aminoborane (H(2)N═BH(2)) as a species that can be released in appreciable quantities with the other major impurity, borazine. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) was used to identify the chemical states present in the solid phase material after each stage of decomposition. The boron nitride product was examined for composition, structure, and morphology using scanning Auger microscopy (SAM), powder X-ray diffraction (XRD), and field emission scanning electron microscopy (FESEM). Thermogravimetric Analysis-Mass Spectroscopy (TGA-MS) and Differential Scanning Calorimetry (DSC) were used to identify the onset temperature of the first two mass loss events.

Hydrothermal Synthesis and Structure of a Potassium Tantalum Defect Pyrochlore.

The synthesis and crystal structure of potassium tantalate (KTa(2)(O,OH)(6).1.8H(2)O) with a defect pyrochlore structure are reported. The compound was crystallized directly from tantalum pentoxide in basic solution under hydrothermal conditions at temperatures as low as 200 degrees C. Ion exchange of this substance in acid yielded an H-type defect pyrochlore. Both highly crystalline K-type and H-type materials absorb argon and have BET surface areas of about 14 m(2)/g. The crystal structures were refined by the Rietveld least-squares method from powder X-ray diffraction data. The final R(wp) and chi(2) were 7.70% and 2.79, respectively. The high thermal stability and control of acidity of these materials, along with the simple and cheap synthesis, may find many applications in sorption, catalysis, and microelectronics.