1.
ACS Appl Mater Interfaces ; 6(21): 18832-43, 2014 Nov 12.
Article in English | MEDLINE | ID: mdl-25325388

ABSTRACT

Thermoset/carbon nanotube (CNT) sheet nanocomposites were successfully fabricated by resistive heating assisted infiltration and cure (RHAIC) of the polymer matrix resin. Resistive heating takes advantage of the electrical and thermal conductivity of CNTs to rapidly and uniformly introduce heat into the CNT sheet. Heating the CNT sheet reduces the viscosity of the polymer resin due to localized temperature rise in close proximity to the resin, which enhances resin flow, penetration, and wetting of the CNT reinforcement. Once the resin infusion process is complete, the applied power is increased to raise the temperature of the CNT sheet, which rapidly cures the polymer matrix. Tensile tests were used to evaluate the mechanical properties of the processed thermoset/CNT sheet nanocomposites. The improved wetting and adhesion of the polymer resin to the CNT reinforcement yield significant improvement of thermoset/CNT nanocomposite mechanical properties. The highest specific tensile strength of bismaleimide(BMI)/CNT sheet nanocomposites was obtained to date was 684 MPa/(g/cm(3)), using 4 V (2 A) for resin infiltration, followed by precure at 10 V (6 A) for 10 min and post curing at 240 °C for 6 h in an oven. The highest specific Young's modulus of BMI/CNT sheet nanocomposite was 71 GPa/(g/cm(3)) using resistive heating infiltration at 8.3 V (4.7 A) for 3 min followed by resistive heating cure at 12.5 V (7 A) for 30 min. In both cases, the CNT sheets were stretched and held in tension to prevent relaxation of the aligned CNTs during the course of RHAIC.

2.
ACS Appl Mater Interfaces ; 5(17): 8597-606, 2013 Sep 11.
Article in English | MEDLINE | ID: mdl-23981043

ABSTRACT

Practical approaches are needed to take advantage of the nanometer-scale mechanical properties of carbon nanotubes (CNTs) at the macroscopic scale. This study was conducted to elucidate the salient factors that can maximize the mechanical properties of nanocomposites fabricated from commercially available CNT sheets. The CNT sheets were modified by stretching to improve CNT alignment and in situ polymerization using polyaniline (PANI), a π-conjugated conductive polymer, as a binder. The resulting CNT nanocomposites were subsequently postprocessed by hot pressing and/or high temperature treatment to carbonize the PANI as a means to improve mechanical properties. The PANI/CNT nanocomposites demonstrated significant improvement in mechanical properties compared to pristine CNT sheets. The highest specific tensile strength of PANI/stretched CNT nanocomposite was 484 MPa/(g/cm3), which was achieved in a sample with ∼42 wt % of PANI. This specimen was fabricated by in situ polymerization followed by hot pressing. The highest specific Young's modulus of 17.1 GPa/(g/cm3) was measured on a sample that was hot-pressed and carbonized. In addition, the highest DC-electrical conductivity of 621 S/cm was obtained on a sample prepared by in situ polymerization of PANI on a stretched CNT sheet.