Inductive Heating of Ceramic Matrix Composites (CMC) for High-Temperature Applications.

The inductive heating of a CMC susceptor for industrial applications can generate very high process temperatures. Thus, the behavior of a silicon carbide-based matrix with carbon-fiber-reinforced carbon (C/C-SiC) as a susceptor is investigated. Specifically, the influence of fiber length and the distribution of carbon fibers in the composite were investigated to find out the best parameters for the most efficient heating. For a multi-factorial set of requirements with a combination of filling levels and fiber lengths, a theoretical correlation of the material structure can be used as part of a digital model. Multi-physical simulation was performed to study the behavior of an alternating magnetic field generated by an inducing coil. The simulation results were verified by practical tests. It is shown that the inductive heating of a C/C-SiC susceptor can reach very high temperatures in a particularly fast and efficient way without oxidizing if it is ensured that a silicon carbide-based matrix completely encloses the fibers.

Effects of Process Parameters in Thermoforming of Unidirectional Fibre-Reinforced Thermoplastics.

Process-induced defects during thermoforming are widespread problems in laminate manufacturing. The aim of this study is to describe the effects of holding time and pressure on several properties of the manufactured laminate. A design of experiments is performed, followed by an analysis of variance to examine significant effects. Subsequently, a regression model is created to predict the laminate's properties, which is also validated. A significant interaction between holding time and pressure is determined for the resulting tensile strength and elongation at break with a p-value of 1.52·10-16 and 0.02, respectively. The highest values of tensile strength and elongation at break are found for low settings of holding time and pressure. The fibre volume fraction is not affected by the process parameters. As holding time and pressure increase, significant fibre misalignment takes place, leading to a decrease of the mechanical properties. The regression model corresponds well with the validation and a tensile strength of 1049 MPa with an elongation at break of 2.3% is reached.