Enhancing the Performance of Rubber with Nano ZnO as Activators.

The vulcanization of rubber is a chemical process to improve the mechanical properties by cross-linking unsaturated polymer chains. Zinc oxide (ZnO) acts as an activator, boosting the rubbers' sulfur vulcanization. Maintaining the level of ZnO content in the rubber compounds as low as possible is desirable, not only for economic reasons but also to reduce the environmental footprint of the process. In this contribution, octylamine (OA) capped ZnO nanoparticles (5 nm diameter), prepared through a thermal decomposition method, were demonstrated to be efficient activators for the sulfur vulcanization of natural rubber, enabling the reduction of the required amount of ZnO as compared to commercial systems. The effect of different ZnO activators (OA capped ZnO/commercial indirect process ZnO) on the curing characteristics, cross-linking densities, and mechanical performance, as well as the thermal behavior of rubber compounds, were investigated. Compared to the commercial indirect process ZnO, OA capped ZnO nanoparticles not only effectively enhanced the curing efficiency of natural rubber but also improved the mechanical performance of the composites after vulcanization. This was interpreted as, by applying the OA capped ZnO nanoparticles, the ZnO levels in rubber compounding were significantly reduced under the industrial vulcanization condition (151 °C, 30 min).

Plasticization Effect of Bio-Based Plasticizers from Soybean Oil for Tire Tread Rubber.

Modified soybean oil (MSO) is synthesized from soybean oil (SO) and sulfur, aiming to reduce the double bond quantity of SO and avoid harmful effects on the crosslink density and mechanical properties of rubber. MSO modified with different weight percentages of sulfur is then used to plasticize tire tread rubber (TR). It is found that the crosslink density and modulus of MSO- plasticized rubber are significantly improved compared with that of SO-plasticized TR. MSO modified with 6 wt % sulfur (MSO-6%) exhibits the best plasticization effect on TR, thus, the plasticization effect of MSO-6% on TR was further studied by adjusting its additive content. Thereafter, the Mooney viscosity, Payne effect, mechanical property of different amount of MSO-6% plasticized TR are studied to investigate their plasticization effect. At the same additive content of plasticizer, the plasticization effect of MSO-6% and a commonly used aromatic hydrocarbon plasticizer (AO) is compared to determine the potential application of MSO on tire tread rubber. It is found MSO shows similar plasticization effect on TR compared with AO. More important, the aging resistance property and wear resistance property of MSO-6% plasticized rubber are better than those of AO-plasticized rubber. Therefore, MSO-6% is a promising bio-based plasticizer for tire tread rubber.