ABSTRACT
In this work, the functionalized covalent organic framework (COF) was prepared via a convenient ball milling process. The aldehyde group terminated COF-F reacted with amino thiadiazole in the ball milling jar under mechanical forces; hence, the thiadiazole functionalized COF-F was obtained and denoted as Thdz@COF-F. The as-prepared Thdz@COF-F serves as an oil-based lubricant additive and exhibits remarkable tribological properties, which can reduce the average friction coefficient of base oil from 0.169 to 0.102 and decrease the wear volume by 87.0%. The antifriction and antiwear performances are mainly due to the repairing effect of Thdz@COF-F nanoparticles and the protective tribo-film that averts the direct contact of friction pairs. In addition, through the ball milling method, triazole and thiazole functionalized COF-F were also prepared and represented good lubrication performance, demonstrating the feasibility of this mechanochemical synthesis method for functionalized COFs.
ABSTRACT
Traditional laser-assisted method (top-down synthesis strategy) is applied in the preparation of carbon dots (CDs) by cutting larger carbon materials, which requires harsh conditions, and the size distribution of the CDs is seldom monodisperse. In this work, heteroatom-doped CDs, represented by N,S co-doped CDs (N,S-CDs), can be prepared successfully by pulsed laser irradiation of heterocyclic aromatic hydrocarbons-based small molecule compound solution. The friction coefficient (COF) of base oil PAO decreases from 0.650 to 0.093, and the wear volume reduces by 92.0% accompanied by 1 wt.% N,S-CDs addition, while the load-bearing capacity is improved from 100 to 950 N. The excellent lubrication performance is mainly attributed to the formation of a robust tribofilm via a tribochemical reaction between N,S-CDs and friction pairs, and the N,S-CDs can play a mending effect and polishing effect for worn surfaces. Furthermore, the lubricant containing heteroatom doped CDs are capable of being prepared in situ via pulsed laser irradiation of heterocyclic aromatic hydrocarbons in base oil, which can avoid the redispersed problem of nano-additive in base oil to maintain long-term dispersion, with COF of 0.103 and low wear volume ≈1.99 × 105 µm3 (76.9% reduction) even after standing for 9 months.
ABSTRACT
The dispersion stability of nano-lubricating additives is crucial for the shelf life of lubricant and its practical applications. Nitrogen-sulfur co-doped carbon dots (N,S@CDs) via a one-step hydrothermal method with nitropyrene and thiourea as raw materials are hereby presented. The N and S elements are selectively distributed throughout the entire carbon skeleton with a doping amount of 22.6 at%. The as-synthesized N,S@CDs exhibit excellent dispersion stability in PEG200 and maintain stability for over one year. The experiment results indicate that N,S@CDs significantly improve the anti-wear and friction reduction properties of PEG200, while the friction coefficient is reduced from 0.25 to 0.09 with 1.5 wt% N,S@CDs addition, and the wear volume, depth, and width are reduced by 68%, 52%, and 57%, respectively. The good lubrication performance is attributed to N,S@CDs excellent dispersion stability, enhanced filling and polishing effects, and complex tribochemical reactions caused by heteroatom doping to form a stable protective film on the worn surface. Furthermore, the as-prepared N,S@CDs exhibit intrinsic fluorescence intensity in PEG200 with the photoluminescence quantum yield (PLQY) of 12.5% and remain fluorescent stable during the long-term friction process, therefore the N,S@CDs have a potential application prospect in non-destructive detection of oil leakage via fluorescence labeling method.