ABSTRACT
Introduction: The overall prevalence of Klebsiella spp., a group of important zoonotic pathogens, in the global dairy herds and the risk of cross-species transmission between humans and dairy cows remain to be clarified. This systematic review aimed to determine the prevalence of Klebsiella spp. in milk samples from dairy cows with mastitis worldwide and to assess the factors influencing the prevalence of these strains. Methods: Qualified studies published from 2007 to 2021 were retrieved from ScienceDirect, Web of Science, PubMed, WanFang Database, China National Knowledge Infrastructure (CNKI), and VIP Chinese Journal Database. Calculations of prevalence and their 95% confidence intervals (CIs) were performed for all the studies using the Freeman-Tukey double arcsine transformation (PFT). Results: A total of 79,852 milk samples from 55 manuscripts were examined in this meta-analysis, and 2,478 samples were found to be positive for Klebsiella spp. The pooled prevalence estimates worldwide were 7.95% (95% CI: 6.07%-10.06%), with significant heterogeneity (I 2 = 98.8%, p = 0). The sampling period of 2013-2020 had a higher (p < 0.05) Klebsiella-positive proportion of milk samples (12.16%, 95% CI: 8.08%-16.90%) than that of 2007-2012 (3.85%, 95% CI: 2.67%-5.21%), indicating that bovine mastitis caused by Klebsiella may become increasingly prevalent. The risk factors for the high prevalence of Klebsiella in milk samples mainly included: economic development level (developing countries; 11.76%, 95% CI: 8.25%-15.77%), mastitis type (CM; 11.99%, 95% CI: 8.62%-15.79%), and population density (>500 per sq km; 10.28%, 95% CI: 2.73%-21.58%). Additionally, a bivariate meta-regression analysis revealed that the multidrug-resistance (MDR) rate of the epidemic strains was also closely related to economic development level (R 2 = 78.87%) and population density (R 2 = 87.51%). Discussion: Due to the potential risk of cross-species transmission between humans and cows, the prevalence of mastitis milk-derived Klebsiella and its high MDR rate need to be monitored, especially in developing countries with high population densities.
ABSTRACT
The application of cast-in-situ phosphogypsum as the wall material of building structures can greatly reduce the environmental pollution caused by phosphogypsum. Through the uniaxial compression test of cast-in-situ phosphogypsum specimens, the compressive strength of cast-in-situ phosphogypsum is determined, the constitutive relationship of the material is drawn up, and the elastic modulus and Poisson's ratio of the material are determined. The results show that when the strain of the specimen is close to the peak strain, the cast-in-situ phosphogypsum has brittle properties and rapidly fails, where the failure state is mainly splitting failure. The retarder has a great influence on the peak stress. When the content of the retarder is about 0.3%, the peak stress is 8.6 MPa and the ultimate strain is 2.54 × 10-3, while the peak stress is 2.8 MPa and the ultimate strain is 2.01 × 10-3. The three segment constitutive fitted equations reflect all the characteristics of the compression specimen. When the strength of the cast-in-situ phosphogypsum is high, the elastic modulus is also high. When the content of the retarder is about 0.3%, the elastic modulus is 5300 MPa, and when the content of retarder is far greater than 0.3%, the elastic modulus is 2000 MPa. The Poisson's ratio of material is recommended as 0.19.