Application of Silicon Nanostructure Arrays for 6-inch Mono and Multi-Crystalline Solar Cell.

In this study, we fabricate uniform silicon nanowire (SiNW) arrays on 6-inch mono- and multi-crystalline wafers by employing the improved solution-processed metal-assisted chemical etching (MacEtch) method. Furthermore, the improved MacEtch can be applied to various crystalline orientation wafers. The SiNW arrays are 470 nm in length with high density; they demonstrate a good optical trapping effect and reflectance well below 6% over a broad wavelength range from 300 to 1100 nm. The improved MacEtch shows no difference in reflectance for a pyramid/SiNW mono-crystalline wafer with appropriate uniformity; the average delta from the center to other positions is within 22%. The effective lifetime is lower for SiNW arrays because the higher surface state causes higher surface recombination.Finally, we make the multi-crystalline wafer into an Al-BSF solar cell device with MacEtch SiNW texture, resulting in an averaged power conversion efficiency of 17.83%, which is higher than that of standard acid-textured solar cell devices. Consequently, the improved MacEtch concept is suitable for commercial mass production in the photovoltaic industry.

Solution-processed carrier selective layers for high efficiency organic/nanostructured-silicon hybrid solar cells.

The reduction of interface minority carrier recombination is regarded as a key performance indicator in improving the power conversion efficiency (PCE) of organic-inorganic hybrid solar cells. In this study, we chose two kinds of carrier-selective layers to be applied in a hybrid solar cell device. A hole selective transporting layer of N,N'-bis(3-methylphenyl)-N,N'-diphenylbenzidine (TPD) was added to the interface between Si nanohole structures and PEDOT: PSS, and the electron selective layer cesium carbonate (Cs2CO3) was added to the interface between the backside Si wafer and the rear Ti/Ag electrode. The main process used a clean and low-cost solution process, and the annealed temperature was under 140 °C. In addition, after we inserted these two carrier selective layers, the minority carrier lifetime was prolonged from 29.98 µs to 140.81 µs, indicating its significance in reducing the recombination rate. Eventually, we demonstrated that the PCE of Si/organic heterojunction solar cells can be improved to 13.23%.

Low-Pressure-Assisted Coating Method To Improve Interface between PEDOT:PSS and Silicon Nanotips for High-Efficiency Organic/Inorganic Hybrid Solar Cells via Solution Process.

Nanostructured silicon hybrid solar cells are promising candidates for a new generation photovoltaics because of their light-trapping abilities and solution processes. However, the performance of hybrid organic/Si nanostructure solar cells is hindered because of carrier recombination at surface and poor coverage of organic material poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) ( PEDOT: PSS) on nanostructures. Here we demonstrate low-pressure-assisted coating method of PEDOT: PSS on surface-modified silicon nanotips with broadband light-trapping characteristics to improve interface property and to achieve high-efficiency hybrid solar cells through a solution process. The approach enhances the effective minority-carrier lifetime and the coverage of PEDOT: PSS on the surface of nanostructures. Hybrid solar cells fabricated with surface-modified nanotips exhibit a high fill factor of 70.94%, short-circuit current density of 35.36 mA/cm(2), open-circuit voltage of 0.528 V, and power conversion efficiency of 13.36%. The high efficiency and the high fill factor are achieved because of conformal coating of PEDOT: PSS via a low-pressure-assisted coating process, excellent light harvesting without sacrificing the minority-carrier lifetime, and efficient charge separation/collection of photogenerated carriers.