Tailoring the chain packing in ultrathin polyelectrolyte films formed by sequential adsorption: nanoscale probing by positron annihilation spectroscopy.

Depth profiling experiments by positron annihilation spectroscopy have been used to investigate the free volume element size and concentration in films assembled using the layer-by-layer (LbL) adsorption method. Films prepared from strong polyelectrolytes, weak polyelectrolytes, hydrogen-bonding polymers, and blended polyelectrolyte multilayers have different chain packing that is reflected in the free volume characteristics. The influence of various parameters on free volume, such as number of bilayers, salt concentration, solution pH, and molecular weight, has been systematically studied. The free volume cavity diameters vary from 4 to 6 Å, and the free volume concentrations vary from (1.1-4.3) × 10(20) cm(-3), depending on the choice of assembly polymers and conditions. Films assembled from strong polyelectrolytes have fewer free volume cavities with a larger average size than films prepared from weak polyelectrolytes. Blending the weak polyanion poly(acrylic acid), PAA, with the strong polyanion poly(styrene sulfonate), PSS, to layer alternately with the polycation poly(allyamine hydrochloride), PAH, is shown to be a viable method to achieve intermediate free volume characteristics in these LbL films. An increase in salt concentration of the adsorption solutions for films prepared from strong polyelectrolytes makes these films tend toward weaker polyelectrolyte free volume characteristics. Hydrogen-bonded layered films show larger free volume element size and concentration than do their electrostatically bonded counterparts, while reducing the molecular weight of these hydrogen-bonded polymers results in slightly reduced free volume size and concentration. A study of the effect of solution pH on films prepared from weak polyelectrolytes shows that when both polyelectrolytes are substantially charged in solution (assembly pH = 7.5), the chains pack similarly to strong polyelectrolytes (i.e., lower free volume concentration), but with smaller average cavity sizes. These results give, for the first time, a clear indication of how the free volume profile develops in LbL thin films, offering numerous methods to tailor the Ångström-scale free volume properties by judicious selection of the assembly polymers and conditions. These findings can be potentially exploited to tailor the properties of thin polymer films for applications spanning membranes, sensing, and drug delivery.

Click-engineered, bioresponsive, drug-loaded PEG spheres.

A click-chemistry approach to synthesize bioresponsive poly(ethylene glycol acrylate) particles is described. The particles are loaded with a model anticancer drug (doxorubicin, DOX), and undergo simultaneous particle deconstruction and DOX release upon specific activation by the simulated environment of the cellular cytoplasm.

Synthesis, multilayer film assembly, and capsule formation of macromolecularly engineered acrylic acid and styrene sulfonate block copolymers.

We report the use of copolymers synthesized with specific block ratios of weakly and strongly charged groups for the preparation of stable, pH-responsive multilayers. In this study, we utilized reversible addition-fragmentation chain transfer (RAFT) polymerization in the synthesis of novel pH-sensitive copolymers comprising block domains of acrylic acid (AA) and styrene sulfonate (SS) groups. The PAA x- b-SS y copolymers, containing 37%, 55%, and 73% of AA groups by mass (denoted as PAA 37- b-SS 63, PAA 55- b-SS 45, and PAA 73- b-SS 27, respectively), were utilized to perform stepwise multilayer assembly in alternation with poly(allylamine hydrochloride), PAH. The ratio of AA to SS groups, and the effect of the pH of both anionic and cationic adsorption solutions, on multilayer properties, were investigated using ellipsometry and atomic force microscopy. The presence of SS moieties in the PAA x- b-SS y copolymers, regardless of the precise composition, lead to films with a relatively consistent thickness. Exposure of these multilayers to acidic conditions postassembly revealed that these multilayers do not exhibit the characteristic large swelling that occurs with PAA/PAH films. The film stability was attributed to the presence of strongly charged SS groups. PAA x- b-SS y/PAH films were also formed on particle substrates under various adsorption conditions. Microelectrophoresis measurements revealed that the surface charge and isoelectric point of these core-shell particles are dependent on assembly pH and the proportion of AA groups in PAA x- b-SS y. These core-shell particles can be used as precursors to hollow capsules that incorporate weak polyelectrolyte functionality. The role of AA groups in determining the growth profile of these capsules was also examined. The multilayer films prepared may find applications in areas where pH-responsive films are required but large film swelling is unfavorable.

Colloid surface engineering via deposition of multilayered thin films from polyelectrolyte blend solutions.

Multilayer thin films were constructed on polystyrene colloidal particles by depositing alternating layers of poly(allylamine hydrochloride) (PAH) at pH 7.5 and varying composition blends of poly(acrylic acid) (PAA) and poly(styrenesulfonate) (PSS) at pH 3.5. Following the deposition of each layer, microelectrophoresis experiments showed alternating zeta-potentials, suggesting the formation of multilayered films on the particles. Scanning and transmission electron microscopy were used to examine the surface morphology of the colloidal particles, with homogeneous surface coatings apparent for films deposited from PAA/PSS blend solutions containing up to 90 wt % PAA. The colloidal stability of these particles is greater than those coated with individual PAH and PAA layers. In the case of the blend PAA/PSS = 25:75 wt %, up to 20 layers were assembled without compromising the colloidal stability of the dispersion. The results demonstrate that the deposition of layers from PE blend solutions containing a strong and weak PE can be used as a facile method for controlling the surface properties and hence the colloidal stability of core-shell particles, as well as the thickness and morphology of the coatings. Control of these parameters is important for subsequent processing and application of these particles in controlled delivery, photonics, catalytic, and separation applications.