High-energy Er-doped fiber laser with high conversion efficiency is reported, which is mode-locked by a germanium telluride (GeTe)-based saturable absorber (SA). By adjusting the direction of the polarization controller (PC), a high-energy pulse with a central wavelength of 1533.1 nm and a fundamental repetition frequency of 1.58 MHz is achieved. Under the pump power of 450.1 mW, the maximum average output power is 50.48 mW, and the single-pulse energy is 32 nJ. It is worth noting that the optical-to-optical conversion efficiency has reached about 11.2%. The experimental results indicate that GeTe performs excellently as SAs for obtaining mode-locked fiber lasers and plays an extremely important role in high-energy fiber lasers.
ABSTRACT
In this paper, an indium antimonide (InSb) saturable absorber (SA) was successfully fabricated. The saturable absorption properties of the InSb SA were studied, and they show a modulation depth and a saturable intensity of 5.17% and 9.23M W/c m 2, respectively. By employing the InSb SA and building the ring cavity laser structure, the bright-dark soliton operations were successfully obtained by increasing the pump power to 100.4 mW and adjusting the polarization controller. As the pump power increased from 100.4 to 180.3 mW, the average output power increased from 4.69 to 9.42 mW, the corresponding fundamental repetition rate was 2.85 MHz, and the signal-to-noise ratio was 68 dB. The experimental results show that InSb with excellent saturable absorption characteristics can be used as a SA to obtain pulse lasers. Therefore, InSb has important potential in fiber laser generation, further applications in optoelectronics, laser distance ranging, and optical fiber communication, and it can be widely developed.
ABSTRACT
In this work, we fabricate a saturable absorber based on GeTe with saturation intensity and modulation depth of 12.6M W/c m 2 and 7%, respectively. We obtain stable conventional soliton and stretched soliton mode-locking operation. For the conventional soliton state, the average output power increased from 0.93 to 8.70 mW with the increase of pump power, and the fundamental repetition rate was 7.8351 MHz. Its central wavelength and 3 dB bandwidth were 1564.72 and 4.78 nm, respectively. For the stretched soliton state, when the pump power was increased from 87.4 to 420.3 mW, the average output power increased from 2.05 to 10.46 mW. When the maximum average output power reached 10.46 mW, the maximum average single-pulse energy was 0.86 nJ. The experimental results show that GeTe nanosheets will have broad application potential in the field of ultrafast photonics.