ABSTRACT
Appropriate control of substrate surface properties prior to inkjet printing could be employed to improve the printing quality of fine resolution structures. In this paper, novel methods to fabricate patterned surfaces with a combination of hydrophilic and hydrophobic properties are investigated. The results of inkjet printing of PEDOT/PSS conductive ink on these modified surfaces are presented. Selective wetting was achieved via a two-step hydrophilic-hydrophobic coating of 3-aminopropyl trimethoxysilane (APTMS) and 3M electronic grade chemical respectively on PET surfaces; this was followed by a selective hydrophilic treatment (either atmospheric O2/Ar plasma or UV/ozone surface treatment) with the aid of a Nickel stencil. Hydrophobic regions with water contact angle (WCA) of 105° and superhydrophilic regions with WCA <5° can be achieved on a single surface. During inkjet printing of the treated surfaces, PEDOT/PSS ink spread spontaneously along the hydrophilic areas while avoiding the hydrophobic regions. Fine features smaller than the inkjet droplet size (approximately 55 µm in diameter) can be successfully printed on the patterned surface with high wettability contrast.
ABSTRACT
A gecko's superb ability to adhere to surfaces is widely credited to the large attachment area of the hierarchical and fibrillar structure on its feet. The combination of these two features provides the necessary compliance for the gecko toe-pad to effectively engage a high percentage of the spatulae at each step to any kind of surface topography. With the use of multi-tiered porous anodic alumina template and capillary force assisted nanoimprinting, we have successfully fabricated a gecko-inspired hierarchical topography of branched nanopillars on a stiff polymer. We also demonstrated that the hierarchical topography improved the shear adhesion force over a topography of linear structures by 150%. A systematic analysis to understand the phenomenon was performed. It was determined that the effective stiffness of the hierarchical branched structure was lower than that of the linear structure. The reduction in effective stiffness favored a more efficient bending of the branched topography and a better compliance to a test surface, hence resulting in a higher area of residual deformation. As the area of residual deformation increased, the shear adhesion force emulated. The branched pillar topography also showed a marked increase in hydrophobicity, which is an essential property in the practical applications of these structures for good self-cleaning in dry adhesion conditions.