ABSTRACT
Four phthalocyanine derivatives with different electron donor and acceptor substituents (B1, B2, B3, and B4) were synthesized by a solid-phase melting method. The influence of substituent type on the nonlinear optical properties of the materials was investigated in detail. In the case of similar conjugated structures, B3, which has amino electron-donor groups, presents high intramolecular charge transfer, a low energy gap (2.05â eV), and good nonlinear optical properties. Compared with B3, B4 has a larger π-conjugated structure and its energy gap is 0.04â eV smaller. Moreover, B4 has stronger reverse saturation absorption (7 × 10-12 m/W) and optical limiting performance. The four phthalocyanine derivatives exhibit third harmonic generation (THG) characteristics. Furthermore, the third harmonic strengths of B1, B2, B3, and B4 are 4 times, 9 times, 11 times, and 21 times that of SiO2, respectively. So, B4 has the best application potential in laser protection and frequency conversion.
ABSTRACT
The pyrene derivative (PD) was synthesized with pyrene-1-carboxaldehyde and p-aminoazobenzene by a Schiff base reaction. Then the obtained PD was dispersed in polyurethane (PU) prepolymer to prepare polyurethane/pyrene derivative PU/PD materials with good transmittance. The nonlinear optical (NLO) performances of the PD and PU/PD materials were studied by the Z-scan technique under picosecond and femtosecond laser pulses. The PD has reverse saturable absorption (RSA) properties under the excitation of 532 nm 15 ps pulses, 650 and 800 nm 180 fs pulses, and a low optical limiting (OL) threshold (0.01J/c m 2). The PU/PD has a larger RSA coefficient than that of the PD under 532 nm 15 ps pulses. With the enhanced RSA, the PU/PD materials exhibit excellent OL (OL) performance. Good NLO properties, high transparency, and easy processing performances make the PU/PD an excellent choice for use in OL and laser protection fields.
ABSTRACT
Two pyrenyl Schiff base derivatives with π conjugated structures (B2 and B3) were designed and synthesized. Then, B2 and B3 were added into polyurethane to obtain doped and bonded polyurethane nonlinear optical materials (B2/PU and B3/PU), respectively. The synthesized B2, B3, and polyurethane nonlinear optical materials were tested by a nanosecond (ns) and picosecond (ps) pulse Z-scan at a 532 nm wavelength. Due to the two-photon absorption-induced excited state absorption (TPA-ESA), B2, B3, and polyurethane nonlinear optical materials show reverse saturable absorption (RSA). From a quantum chemistry calculation, it can be concluded that the RSA of B2 and B3 comes from the large π conjugated system and intramolecular charge transfer. Furthermore, B2, B3, and the polyurethane nonlinear optical materials show good optical limiting. B2/PU and B3/PU not only have excellent nonlinear optical properties but also have good transmittance, thermal stability, and processability of polyurethane materials. The combination of pyrenyl Schiff base derivatives and polyurethane materials greatly improves the application of nonlinear small molecules in the field of optical limiting and all-optical switching.