Residual Fatigue Properties of Asphalt Pavement after Long-Term Field Service.

Asphalt pavement is widely used for expressways due to its advantages of flexibility, low cost, and easy maintenance. However, pavement failures, including cracking, raveling, and potholes, will appear after long-term service. This research evaluated the residual fatigue properties of asphalt pavement after long-term field service. Fatigue behavior of specimens with different pavement failure types, traffic load, service time, and layers were collected and characterized. Results indicate that after long-term field service, surface layer has a longer fatigue life under small stress levels, but shorter fatigue life under large stress levels. Longer service time results in greater sensitivity to loading stress, while heavier traffic results in shorter fatigue life. Surface and underneath layers present very close fatigue trend lines in some areas, indicating that the fatigue behavior of asphalt mixture in surface and underneath layers are aged to the same extent after eight to ten years of field service.

Evaluation of Fine Aggregate Morphology by Image Method and Its Effect on Skid-Resistance of Micro-Surfacing.

Micro-surfacing is a widely used pavement preventive maintenance technology used all over the world, due to its advantages of fast construction, low maintenance cost, good waterproofness, and skid-resistance performance. This study evaluated the fine aggregate morphology and surface texture of micro-surfacing by AIMS (aggregate image measurement system), and explored the effect of aggregate morphology on skid-resistance of single-grade micro-surfacing. Sand patch test and British pendulum test were also used to detect skid-resistance for comparison with the image-based method. Wet abrasion test was used to measure skid-resistance durability for feasibility verification of single-grade micro-surfacing. The results show that the effect of Form2D on the skid-resistance of micro-surfacing is much stronger than that of angularity. Combining the feasibility analysis of durability and skid-resistance, 1.18⁻2.36 grade micro-surfacing meets the requirements of durability and skid-resistance at the same time. This study also determined that, compared with British pendulum test, the texture result obtained by sand patch test fits better with results of image method.