Deeply Discharged, Quiescently Stable, and Long-Life Zn Anode by Spontaneous SEI Formation.

Zn ion batteries (ZIBs) are a promising candidate in safe and low-cost large-scale energy storage applications. However, significantly deteriorated cycling stability of Zn anode in high depth of charge or after long-term quiescence impedes the practical application of ZIBs. Aiming at the above issue, a spontaneous solid electrolyte interphase (SEI) formation of Zn4(OH)6SO4·xH2O (ZHS) on Zn powder is achieved in pure ZnSO4 electrolyte by facile and rational interface design. The stable and ultrathin ZHS SEI plays a crucial part in insulating water molecules and conducting Zn2+ ions, intrinsically suppressing the severe hydrogen evolution and dendrite formation on the Zn powder anode. The ZHS-Zn anode delivers a stable cycling at a high DOD of 50% for over 500 h, as well as a lifespan of over 200 h after 40-days of resting at a DOD of 25%. Benefiting from the high utilization of Zn anode, the energy density of the Zn-MnxV2O5 full cell is up to 118 Wh Kg-1. This facile method can fabricate the ZHS-Zn anode as long as 1 m, revealing its feasibility in large-scale production and commercialization.

An Ultrahigh Rate and Stable Zinc Anode by Facet-Matching-Induced Dendrite Regulation.

Resource-abundant metal (e.g., zinc) batteries feature intrinsic advantages of safety and sustainability. Their practical feasibility, however, is impeded by the poor reversibility of metal anodes, typically caused by the uncontrollable dendrite enlargement. Significant effort is exerted to completely prevent dendrites from forming, but this seems less effective at high current densities. Herein, this work presents an alternative dendrite regulation strategy of forming tiny, homogeneously distributed, and identical zinc dendrites by facet matching, which effectively avoids undesirable dendrite enlargement. Confirmed by multiscale theoretical screening and characterization, the regularly exposed Cu(111) facets at the ridges of a copper nanowire are capable of such dendrite regulation by forming a low-mismatched Zn(002)/Cu(111) interface. Consequently, reversible zinc electroplating/stripping is achieved at an unprecedentedly high rate of 100 mA cm-2 for over 30 000 cycles, corresponding to an accumulative areal capacity up to 30 Ah cm-2 . A full cell using this anode shows a high capacity of 308.3 mAh g-1 and a high capacity retention of 91.4% after 800 cycles. This strategy is also viable for magnesium and aluminum anodes, thus opening up a promising and universal avenue toward long-life and high-rate metal anodes.