ABSTRACT
Dependence of the superconducting transition temperature (T(c)) and critial superconducting pressure (P(c)) of the pressure-induced superconductor ß-(BDA-TTP)(2)I(3) [BDA-TTP = 2,5-bis(1,3-dithian-2-ylidene)-1,3,4,6-tetrathiapentalene] on the orientation of uniaxial strain has been investigated. On the basis of the overlap between the upper and lower bands in the energy dispersion curve, the pressure orientation is thought to change the half-filled band to the quarter-filled one. The observed variations in T(c) and P(c) are explained by considering the degree of application of the pressure and the degree of contribution of the effective electronic correlation at uniaxial strains with different orientations parallel to the conducting donor layer.
ABSTRACT
A pressure transmitting medium named Daphne 7474, which solidifies at P(s)=3.7 GPa at room temperature, is presented. The value of P(s) increases almost linearly with temperature up to 6.7 GPa at 100 degrees C. The high pressure realized by a medium at the liquid state allows a higher limit of pressurization, which assures an ideal hydrostatic pressure. We show a volume change against pressure, pressure reduction from room to liquid helium temperature in a clamped piston cylinder cell, pressure distribution and its standard deviation in a diamond anvil cell, and infrared properties, which might be useful for experimental applications.
ABSTRACT
The 2:1 salts of a new donor molecule, EDT-DSDTFVO with MX4- (M = Fe, Ga; X = Cl, Br) ions, were prepared. The crystal structures of the donor molecules had a beta-type packing motif. All the salts essentially exhibited metallic behaviors despite the small upturns in the resistances below 30-70 K. A large negative magnetoresistance (MR) effect [-14.7% (rho(perpendicular)) at 4.0 K and 5 T] was observed in the FeCl4- salt, while a positive MR effect [+4.0% (rho(perpendicular)) at 4.0 K and 5 T] was observed in the GaCl4- salt, suggesting that there is a pi-d interaction in the FeCl4- salt. The pressure application suppressed the resistivity upturns, increased the negative MR effect (-17.7% at 9.5 kbar) in the FeCl4- salt, and decreased the positive MR effect (+3.3% at 15 kbar) in the GaCl4- salt.
ABSTRACT
We report the crystal structure and physical properties of the 2:1 FeCl4- salt of a new donor molecule, EDO-TTFVO. Crystal structure analysis of this salt revealed that the donor molecules formed a beta' '-type two-dimensional conducting layer, and there is a short S...Cl contact between the donor molecules and the FeCl4- ions, which is expected to mediate a strong pi-d interaction. This salt showed a stable metallic conducting behavior down to 0.3 K and an antiferromagnetic ordering at TN approximately 3.0 K, indicating that this salt becomes a new antiferromagnetic molecular metal at ambient pressure. The appearance of the magnetic ordering is considered to originate from the strong pi-d interactions between the donor molecules and the FeCl4- ions because the field dependence of magnetoresistances was remarkably affected below the antiferromagnetic transition temperature.