ABSTRACT
This study investigated whether surface topography affects the retentive strength of cemented full crowns, comparing the effects of standard machined, sandblasted, and grooved implant abutments. Five metallic crowns per abutment type were cast and cemented with zinc phosphate. After 24 hours, the specimens were submitted to a tensile test. The retentive strength of the cemented crowns was affected by abutment surface topography. The sandblasted and grooved surface groups had approximately 2.4 times greater mean uniaxial retentive strength than the machined surface group (P < .001). The retentive strength of the sandblasted and grooved abutments was similar, despite marked differences in surface profiles and roughness parameters.
Subject(s)
Cementation/methods , Crowns , Dental Abutments , Dental Implants, Single-Tooth , Dental Prosthesis Design , Dental Prosthesis Retention , Aluminum Oxide/chemistry , Dental Etching/methods , Dental Materials/chemistry , Dental Stress Analysis/instrumentation , Humans , Humidity , Materials Testing , Stress, Mechanical , Surface Properties , Temperature , Tensile Strength , Time Factors , Titanium/chemistry , Zinc Phosphate Cement/chemistryABSTRACT
Introdução: O propósito deste trabalho é descrever os cuidados na confecção do troquel de gesso, pós-moldagem com silicone de adição, com especial atenção ao posicionamento do pino, amiúde realizado displicentemente. Métodos: Para avaliar a alteração dimensional decorrente desse passo na técnica de obtenção do troquel, foi confeccionado um modelo metálico, simulando um preparo dental para coroa total com afastamento gengival. Utilizou-se silicone de adição para as moldagens e os 50 troquéis obtidos em gesso foram divididos em 5 grupos: Grupo A (controle, sem pino), Grupo B (pinos fixados previamente ao preenchimento com gesso), Grupos C, D e E (pinos colocados nos tempos: 5min, 8min e 8min30s, após início da reação de presa do gesso). Os corpos de prova foram mensurados com microscópio comparador (30x, com 0,001mm de precisão. Mitutoyo®). Resultados: A análise estatística (ANOVA e teste Tukey, p≤1%) confirmou as menores alterações dimensionais nos troquéis dos grupos A e B quando comparados aos troquéis dos grupos C, D e E. (As alterações dimensionais foram diretamente proporcionais aos tempos). Conclusões: A introdução do pino durante a presa do gesso induziu a distorções no material de moldagem, resultando em troquéis alterados. Recomenda-se, portanto, que o pino seja posicionado no molde, previamente ao preenchimento com gesso, ou que seja fixado após a presa total do gesso, executando-se um pequeno orifício no gesso, firmando-o com resina acrílica ou cola adesiva.
Introduction: The purpose of this study is to mention precautions of gypsum casts made of addition silicone impression material, specially related to dowel pin's insertion, often carried out recklessly. Methods: In order to investigate the dimensional changes of stone dies, a metal model was made in order to simulate full crown dental preparation and gingival sulcus. Fifty stone die replicas were divided into 5 groups: group A (control, without dowel pin), group B (dowel pin inserted prior to the pouring of the stone), groups C, D and E ( dowel pins were introduced 5 minutes, 8 minutes and 8 minutes and 30 seconds after stone setting reaction, respectively). The specimens were evaluated through a microscope (30X, 0.001mm precision. Mitutoyo®). Results: Statistical analysis (ANOVA and Tukey, p£1%) showed that the smaller alterations took place in the specimens of groups A and B. Conclusion: The insertion of the dowel pin during stone setting induced distortions of the elastomeric impression material, resulting in dimensional alteration of die stone. Thus, it is recommended that the dowel pin be positioned in the impression before stone pouring, or be fixed after stone setting, making a small hole in the stone, firming the dowel pin with acrylic resin.
Subject(s)
Dental Impression Materials , Dental PinsABSTRACT
A desinfecção de moldes dentais é uma maneira de controlar a infecção cruzada entre o consultório odontológico e o laboratório de prótese. Normalmente, é feita com soluções químicas à temperatura ambiente, sendo a imersão a forma mais utilizada pelos profissionais de Odontologia. O presente trabalho teve como finalidade verificar a estabilidade dimensional de moldes de godiva de baixa fusão, imersos por 30 minutos em três soluções desinfetantes de comprovada eficácia antimicrobiana (hipoclorito de sódio a 1%, glutaraldeído a 2% e fenol a 3%) e um detergente enzimático. O grupo controle não foi submetido à ação das soluções químicas. Conclui-se que não houve alteração dimensional significante nos moldes de godiva em nenhuma dessas soluções desinfetantes, exceto para o detergente enzimático.
Subject(s)
Dental Impression Materials , Infection Control , Solutions , Dental Disinfectants , Dental Offices , Infection Control, Dental , Laboratory EquipmentABSTRACT
Este estudo teve como objetivo comparar as tensöes geradas por próteses sobre implantes cimentadas e parafusadas. Constituíram-se 10 próteses, 5 próteses para sistema cimentado e 5 próteses para sitema parafusado. As próteses parafusadas foram testadas com 3 seqüências de aperto: 1) Parafuso central, parafuso esquerdo e parafuso direito. 2) Parafuso esquerdo, parafuso central e parafuso direito. 3) Parafuso direito, parafuso central e parafuso esquerdo. As próteses foram fixadas sobre um modelo confeccionado com resina fotoelástica e as tensões avaliadas segundo as franjas isocromáticas observadas no modelo através do fotopolarímetro. Conclui-se que as próteses cimentadas apresentaram níveis de tensäo maior que as próteses parafusadas, näo tendo influenciado nos resultados a seqüência de aperto dos parafusos
Subject(s)
Dental Implantation, Endosseous , Dental Prosthesis , Prostheses and ImplantsABSTRACT
O propósito deste trabalho é descrever a importância da caracterização de dentes de estoque onde a cor, forma, disposição e alinhamento são levados em consideração na busca de resultados estéticos