Aluminum-Based Metal-Organic Frameworks Derived Al2O3-Loading Mesoporous Carbon as a Host Matrix for Lithium-Metal Anodes.

Li-metal anode attracts great focus owing to its ultra-high specific capacity and the lowest redox potential. However, the uncontrolled growth of Li dendrite leads to severe security issues and limited cycle life. Herein, Al2O3 loading mesoporous carbon (Al2O3@MOF-C) derived from Al-based metal-organic frameworks (Al-MOFs) was investigated as the stable host matrix for Li metal, in which, Al2O3 was served as nano seeds for the Li deposition and decrease the Li nucleation overpotential. Except that, the high specific surface area and wide pore distribution can also buffer the volume changes of Li and fasten electron transfer, hence a dendrite-free morphology was observed even after 50 cycles at 2 mA cm-2. High Li coulombic efficiency of 97.9% after 100 cycles at 1 mA cm-2, 1 mAh cm-2, and 97.6% after 50 cycles at 1 mA cm-2 and 6 mAh cm-2 were performed by Al2O3@MOF-C electrodes. Good performances were also obtained for Li-sulfur and LiFePO4 batteries. The performances of Al2O3@MOF-C@Li were compared with Li foil and Cu@Li in full cell configurations. The electrochemical tests of full cells based on Al2O3@MOF-C@Li indicated that this Al-based functional host matrix can enhance the Li-utilization and lead to significant enhancement of the cycling performance of Li anodes.

A Natural Biopolymer Film as a Robust Protective Layer to Effectively Stabilize Lithium-Metal Anodes.

Li metal is considered as an ideal anode for Li-based batteries. Unfortunately, the growth of Li dendrites during cycling leads to an unstable interface, a low coulombic efficiency, and a limited cycling life. Here, a novel approach is proposed to protect the Li-metal anode by using a uniform agarose film. This natural biopolymer film exhibits a high ionic conductivity, high elasticity, and chemical stability. These properties enable a fast Li-ion transfer and feasiblity to accomodate the volume change of Li metal, resulting in a dendrite-free anode and a stable interface. Morphology characterization shows that Li ions migrate through the agarose film and then deposit underneath it. A full cell with the cathode of LiFPO4 and an anode contaning the agarose film exhibits a capacity retention of 87.1% after 500 cycles, much better than that with Li foil anode (70.9%) and Li-deposited Cu anode (5%). This study provides a promising strategy to eliminate dendrites and enhance the cycling ability of lithium-metal batteries through coating a robust artificial film of natural biopolymer on lithium-metal anode.